强磁场下冷却速度对fe--0.12%c合金显微组织的影响
Keywords: 金属材料,强磁场,扩散型固态相变,铁碳合金,珠光体,冷却速度
Abstract:
？研究了强磁场(12t)下冷却速度对fe--0.12%c合金中的珠光体组织形貌的影响.结果表明:强磁场下珠光体团的长轴方向与磁场方向平行且伸长的程度随其冷却速度的提高而减弱.板平面平行于磁场方向比垂直于磁场方向放置的试样的珠光体面积分数低,同时珠光体团长轴方向与磁场方向平行且伸长的程度也低.最后,探讨了强磁场下珠光体组织形貌的演变机理.
| [1] | 4j.k.choi,h.ohtsuka,y.xu,effectsofstrongmagneticfieldonthephasestabilityofplaincarbonsteel,scriptamater.,43,221(2000)
|
| [2] | 5haoxijiang,h.ohtsuka,effectofhighmagneticfieldonphasetransformationtemperatureandmicrostructureoffe–basedalloys,journalofmaterialsandmetallurgy,4(21),32(2005)
|
| [3] | 6haoxijiang,h.ohtsuka,effectofhighmagneticfieldonphasetransformationtemperatureinfe–calloys,materialstransactions,45(8),2622(2004)
|
| [4] | 7zhangyudong,hechangshu,zhaoxiang,c.esling,zuoliang,anewapproachforrapidannealingofmediumcarbonsteels,adv.eng.mater.,6(5),310(2004)
|
| [5] | 8haoxijiang,h.ohtsuka,p.rango,quantitativecharacterizationofthestructuralalignmentinfe–0.4calloytransformedinhighmagneticfield,mater.trans.,44,211(2003)
|
| [6] | 9haoxijiang,h.ohtsuka,h.wada,structuralelongationandalignmentinafe–0.4calloybyisothermalferritetransformationinhighmagneticfields,mater.trans.,44,2532(2003)
|
| [7] | 10zhangyudong,hechangshu,zhaoxiang,newmicrostructuralfeaturesoccurringduringtransformationfromaustenitetoferriteunderthekineticinfluenceofmagneticfieldinamediumcarbonsteel,j.mag.mag.mater.,284,287(2004)
|
| [8] | 11h.ohtsuka,y.xu,j.k.choi,diffusiontransformationbehaviourandstructureinhighmagneticfield,in:the3rdinternationalsymposiumonepm,(nagoya,theironandsteelinstituteofjapan,2000)p.596
|
| [9] | 12wucunyou,litingju,wenbin,jinjunze,ferritetransformationinspheroidalgraphitecastironunderahighmagnetiefield,j.mater.science,39,1129(2004)
|
| [10] | 13r.a.jaramillo,s.s.babu,g.m.ludtka,effectof30tmagnetidfieldontransformationsinanovelbainiticsteel,scriptamater.,52,461(2005)
|
| [11] | 1m.shimotomai,k.maruta,k.mine,m.matsui,formationofalignedtwo–phasemicrostructurebyapplyingamagneticfieldduringtheaustenitetoferritetransformationinsteels,actamater.,51,2921(2003)
|
| [12] | 2m.shimotomai,k.maruta,alignedtwo–phasestructureinfe–calloys,scriptamater.,42(5),499(2000)
|
| [13] | 3h.ohtsuka,y.xu,h.wada,alignmentofferriteofgrainsduringaustenitetoferritetransformationinahighmagneticfield,mat.trans.jim,41(8),907(2000)
|
| [14] | 14zhangyudong,c.esling,gongminglong,g.vincent,zhaoxiang,zuoliang,microstructuralfeaturesinducedbyahighmagneticfieldinahypereutectoidsteelduringausteniticdecomposition,scriptamater.,54,1897(2006)
|
| [15] | 15e.e.underwood,quantitativemicroscopy(newyork,mcgraw–hill,1968)p.104
|
| [16] | 16j.crangle,themagneticpropertiesofsolids(london,edwardarnold(publishers)ltd,1977)p.16
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|