铋纳米线和纳米片的制备
Keywords: 半金属材料,？铋纳米线,？铋纳米片,？模板效应,体膨胀系数
Abstract:
？通过调控水和乙二胺溶液的组份控制产物的形貌和结构,制备了铋纳米线和铋纳米片,研究了组份变化对产物形貌结构的影响,并依此提出了乙二胺模板效应以及由乙二胺引起的从动力学向热力学转换控制晶体生长的生长机制。铋纳米线的体膨胀系数随着温度的升高减小,并在一转变温度(455℃左右,低于块体的转变温度)变为负值。
| [1] | 7xingkaiduan,junyouyang,wenzhu,xi’anfan,structureandelectricalpropertiesofbismuththinfilmspreparedbyflashevaporationmethod,mater.lett.,61(22),4341(2007)
|
| [2] | 8junweiwang,xunwang,qingpeng,yadongli,synthesisandcharacterizationofbismuthsingle-crystallinenanowiresandnanospheres,inorg.chem.,43(23),7552(2004)
|
| [3] | 9j.wang,y.li,rationalsynthesisofmetalnanotubesandnanowiresfromlamellarstructures,adv.mater.,15(5),445(2003)
|
| [4] | 10l.li,y.zhang,y.w.yang,x.h.huang,g.h.li,l.d.zhang,diameter-dependedthermalexpansionpropertiesofbinanowirearrays,appl.phys.lett.,87(3),031912(2005)
|
| [5] | 11liangli,yongzhang,guanghaili,lidezhang,aroutetofabricatesinglecrystallinebismuthnanowirearrayswithdifferentdiameters,chem.phys.lett.,378(3–4),244(2003)
|
| [6] | 1m.r.black,p.l.hagelstein,s.b.cronin,y.m.lin,m.s.dresselhaus,opticalabsorptionfromanindirecttransitioninbismuthnanowires,phys.rev.b.,68(23),235417(2003)
|
| [7] | 2y.m.lin,s.b.cronin,y.y.jackie,m.s.dresselhaus,j.p.heremans,transportpropertiesofbinanowirearrays,appl.phys.lett.,76(26),3944(2000)
|
| [8] | 3b.o’brien,m.plaza,l.y.zhu,l.perez,c.l.chien,p.c.searson,magnetotransportpropertiesofelectrodepositedbismuthfilms,j.phys.chem.,c,112(31),12018(2008)
|
| [9] | 4j.p.heremans,c.m.thrush,d.t.morelli,thermoelectricpowerofbismuthnanocomposites,phys.rev.lett.,88(21),216801(2002)
|
| [10] | 5junweiwang,guanghancao,yadongli,giantpositivemagnetoresistanceinnon-magneticbismuthnanoparticles,mater.res.bull.,38(11-12),1645(2003)
|
| [11] | 6yanbaozhao,zhijunzhang,hongxindang,asimplewaytopreparebismuthnanoparticles,mater.lett.,58(5),790(2004)
|
| [12] | 12c.j.tang,y.x.zhang,g.z.wang,h.q.wang,g.h.li,fabricationofurchin-likebismuthnanostructuresviaafacilesolvothermalroute,chem.lett.,37(7),722(2008)
|
| [13] | 13xiaohuhuang,guanghaili,bingqiangcao,mingwang,changyihao,morphologyevolutionandclpropertyofni-dopedzincoxidenanostructureswithroomtemperatureferromagnetism,j.phys.chem.c,113(11),4381(2009)
|
| [14] | 14xiaohuhuang,yonggangzhu,xincundou,guanghaili,tuningpeculiarantimonymicro-andnano-morphologyviaanovelelectrodepositionapproach,mater.lett.,62(2),249(2008)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|