表面引发接枝聚合法制备凹凸棒土/聚甲基丙烯酸甲酯杂化粒子的研究
DOI: 10.3724/SP.J.1105.2013.12318, PP. 978-984
Keywords: 凹凸棒土,甲基丙烯酸甲酯,氧化-还原引发体系,表面引发接枝聚合,接枝率
Abstract:
将γ-氨丙基三乙氧基硅烷(APTES)接枝到凹凸棒土(AT)表面,制得表面键合伯氨基的改性粒子AT-APTES;通过AT-APTES表面的伯氨基和过硫酸铵(APS)构成氧化-还原引发体系,采用无皂乳液法实现甲基丙烯酸甲酯(MMA)在AT表面接枝聚合,制得最高接枝率为29.4%的杂化粒子AT-g-PMMA;采用红外光谱(FTIR)、拉曼光谱(Raman)、透射电镜(TEM)以及热失重分析(TGA)等方法对杂化粒子AT-g-PMMA进行了表征;研究了主要配方及工艺条件对表面引发接枝聚合接枝率的影响.结果表明,伯氨基-过硫酸铵引发体系可以有效引发MMA在AT表面接枝聚合,由于引发点位于AT表面,故接枝率较高.本研究体系适宜的温度为65℃,单体MMA用量为水质量的6%,APS用量为单体质量的1%,此工艺条件下可有效减小均聚反应对接枝聚合反应的影响.先接枝到AT表面的聚合物对后续的接枝聚合反应产生抑制作用,接枝率越高,抑制作用越大.
| [1] | 4 Mehdi S K,Vahid H A,Farid B S,Saeid R R,Hossein R M.Polym composite,2012,33(2):215~224
|
| [2] | 5 Yang Y,Yan X H.Cui Y,He Q,Li X D,Wang A H,Fei J B.J Mater Chem,2008,18:5731~5737
|
| [3] | 6 Fu Q,Lin W C,Huang J L.Macromolecules,2008,41(7):2381~2387
|
| [4] | 7 Robert M K,William S R,Marcus W.Macromolecules,2004,37:6644~6649
|
| [5] | 8 Voronov A,Shafranska O.Polymer,2003,44:277~281
|
| [6] | 9 Zhang Yanyan(张妍妍),Gao Baojiao(高保娇),Gu Laiyuan(顾来沅),Zhao Xinglong(赵兴龙).Acta Polymerica Sinica(高分子学报),2012,(3):264~271
|
| [7] | 10 Wang Xiaohua(王晓华),Gao Baojiao(高保娇),Wang Mingjuan(王明娟),Fang Xiaolin(房晓琳).Acta Polymerica Sinica(高分子学报),2012,(3):256~263
|
| [8] | 12 Catherine C,Jiang D E,Freédeéric K,Jean P,Fethal I P.Langmuir,2009,25(1):286~293
|
| [9] | 13 Matyjaszewski K.Prog Polym Sci,2005,30:858~875
|
| [10] | 14 Wang Z Q,Zhou Y M,Sun Y Q.J Inorg Organomet Polym,2009,19:202~207
|
| [11] | 1 Bradley W F. Am Mincral,1940,25(6):405~410
|
| [12] | 2 Sanchez C,Beatriz J,Philippe B,Michael P.J Mater Chem,2005,15:3559~3592
|
| [13] | 3 Bogdan Z,Igor L.Macromol Rapid Comm,2011,32(12):859~869
|
| [14] | 11 Limpoco F T,Rigoberto C A,Scott S P,Langmuir,2007,23(24):12196~12201
|
| [15] | 15 Sun Hongxiu(孙洪秀),Cao Qinghua(曹青华),Zhuang Wei(庄伟),Zhang Hongwen(张洪文).Speciality Petrochemicals(精细石油化工),2011,28(5):36~41
|
| [16] | 16 Ngo V G,Bressy C,Leroux C,Margaillan A.Polymer,2009,50:3095~3102
|
| [17] | 17 Tang E J,Cheng G X,Ma X L.Powder Technol,2006,161:209~214
|
| [18] | 18 Feng Xinde(冯新德),Qiu Kunyuan(丘坤元).Science in China(中国科学),1986,B(11):1121~1128
|
| [19] | 19 Feng Xinde(冯新德),Qiu Kunyuan(丘坤元).Polymer Bulletin(高分子通报),2005,(4):23~34
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|