Ag粒子与Ni包覆Ag粒子熔化特性的价键分析
, PP. 673-678
Keywords: Ag纳米粒子,熔化,DV-Xα法
Abstract:
采用非相对论第一原理分子轨道DV-Xα模型簇方法，计算了Ag纳米粒子自由表面与Ag-Ni半共格界面的电子结构，并从键重叠聚居数QAB，层内与层间原子的部分键合强度（PBO）以及界面原子的总键合强度（TBO）几个方面，对Ag的（111），（100）与（110）自由表面和Ag-Ni半共格界面的价健结构进行了比较，进而对其熔化特性进行了分析。初步提示了自由表面“预熔化”与共格界面“过热”的电子机制，并从电子层次上考察了（111），（100）和（110）表面与界面的预熔化与过热程度及其熔化方式。
| [1] | Zhong J, Zhang L H, Jin Z H, Sui M L, Lu K. Acta Mater, 2001; 49: 2897
|
| [2] | Ellis D E, Painter G S. Phys Rev, 1970; 2B: 2887
|
| [3] | Rosen A, Ellis D E, Adachi H, Averill F W. J Chem Phys, 1976; 65: 2639
|
| [4] | Adachi H, Tsukada M, Satoko C. J Phys Soc Jpn, 1978; 45: 875
|
| [5] | Tanaka I, Mizuno M, Nakajyo S, Adachi H. Acta Mater, 1998; 46: 6511
|
| [6] | Mulliken R S. J Chem Phys, 1955; 23: 1833+
|
| [7] | Lindemann F A. Z Phys, 1910; 11: 609
|
| [8] | Born M. i Chem Phys, 1939; 7: 591
|
| [9] | Tallon J L. Nature, 1989; 342: 658
|
| [10] | Fecht H J, Johnson W L. Nature, 1989; 334: 50
|
| [11] | Okamoto P R, Lam N Q, Rchn L E. Solid State Phys, 1999; 52: 1
|
| [12] | Lu K, Li Y. Phys Rev Lett, 1998; 80: 4474
|
| [13] | Jin Z H, Gumbsch P, Lu K, Ma E. Phys Rev Lett, 2001; 87: 055703
|
| [14] | Kofman R, Cheyssac P, Aouaj A L, Lereah Y, Deutscher G, Ben-David T, Penisson J M, Bourret A. Surf Sci, 1994; 303: 231
|
| [15] | Bilalbegovi G. Phys Rev, 1997; 55B: 16450
|
| [16] | Pluis B, Denier van der Gon A W, Frenken J W M, van der Veen J F. Phys Rev Lett, 1987; 59: 2678
|
| [17] | Sheng H W, Ren G, Peng L M, Hu Z Q, Lu K. Philos Mag Lett, 1996; 73: 179
|
| [18] | Sheng H W, Ren G, Peng L M, Hu Z Q, Lu K. J Mater Res, 1997; 12: 119
|
| [19] | Conchmann P R, Jesser W A. Nature, 1977; 269: 481
|
| [20] | Schmidt M, Kusche R, von Issendorff B, Haberland H. Nature, 1998: 393: 238
|
| [21] | Schmidt M, Kusche R, Kronmueller W, von Issendorff B, Haberland H. Phys Rev Lett, 1997; 79: 99
|
| [22] | Daeges J, Gleiter H, Perepezko J H. Phys Lett, 1986, 119A: 79
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|