高NbX80管线钢焊接热影响区显微组织与韧性
DOI: DOI:10.3724/SP.J.1037.2009.00803, PP. 541-546
Keywords: 高Nb,X80管线钢,热输入,热影响区,韧性,马氏体/奥氏体
Abstract:
利用Gleeble-1500模拟不同热输入的单道次焊接热循环过程,通过光学显微镜(OM)、扫描电镜(SEM)及电子背散射衍射(EBSD)对高NbX80管线钢焊接热影响区中的粗晶区(CGHAZ)显微组织、马/奥组元(M/A)形态和分布以及原奥氏体晶粒粗化情况进行研究.结果表明高NbX80管线钢的焊接热输入应不高于30kJ/cm,虽然在高Nb钢中,原奥氏体晶粒的平均尺寸不会随热输入增加过于粗大,但当热输入高于40kJ/cm时,会使得原奥氏体晶粒内粒状贝氏体的晶体取向选择过于单一,大角晶界(≥15o)密度明显降低,有效晶粒尺寸较大,M/A组元也由于热输入过大而明显粗化.上述原因使高NbX80管线钢在大于40kJ/cm热输入条件下热影响区粗晶区韧性明显恶化.
| [1] | Zhong Y, Xiao F R, Zhang J W, Shan Y Y, Wang W, Yang K. Acta Mater, 2006; 54: 435
|
| [2] | Chen C X, Li W S, Wang Q P, Feng B, Liu F M, Xue Z K. J Mater Eng, 2005; 5: 22
|
| [3] | (陈翠欣, 李午申, 王庆鹏, 冯斌, 刘方明, 薛振奎. 材料工程, 2005; 5: 22)
|
| [4] | Li Y, Crowther D N, Green M J W, Mitchell P S, Baker T N. ISIJ Int, 2001; 41: 46
|
| [5] | Zurob H S, Zhu G, Subramanian S V, Purdy G R, Hutchinson C R, Brechet Y. ISIJ Int, 2005; 45: 713
|
| [6] | Zhao M C, Shan Y Y, Xiao F R, Li Y H, Yang K. Mater Sci Technol, 2001; 9: 356
|
| [7] | (李为卫, 刘亚旭, 高惠临, 赵新伟, 冯耀荣, 吉玲康. 焊接学报, 2006; 27: 43)
|
| [8] | Feng Y R, Li H L. Pet Plan Eng, 2005; 9: 1
|
| [9] | (冯耀荣, 李鹤林. 石油规划设计, 2005; 9: 1)
|
| [10] | Zheng L, Fu J Y. Iron Steel, 2006; 41(10): 1
|
| [11] | (郑磊, 付俊岩. 钢铁, 2006; 41(10): 1)
|
| [12] | Miao C L, Shang C J, Cao J P, Wang X M, He X L. Iron Steel, 2009; 44(3): 62
|
| [13] | (缪成亮, 尚成嘉, 曹建平, 王学敏, 贺信莱. 钢铁, 2009; 44(3): 62)
|
| [14] | Lee S, Kim B C, Lee D Y. Scr Metall, 1989; 23: 995
|
| [15] | Hwang B, Kim Y G, Lee S, Kim Y M, Kim N J, Yoo J Y. Metall Mater Trans, 2005; 36A: 2107
|
| [16] | Ohomori Y, Ohtani H, Kunitake T. Metall Sci, 1974; 8: 357
|
| [17] | Naylor J P, Krahe P R. Metall Trans, 1974; 5: 1699
|
| [18] | Lambert A, Garat X, Sturel T, Gourgues A F, Gingell A. Scr Mater, 2000; 43: 161
|
| [19] | (赵明纯, 单以银, 肖福仁, 李玉海, 杨柯. 材料科学与工艺, 2001; 9: 356)
|
| [20] | Diazfuentes M, Izamendia A, Gutierrez I. Metall Mater Trans, 2003; 34A: 2005
|
| [21] | Guo Z, Lee C S, Morris JW. Acta Mater, 2004; 52: 5511
|
| [22] | Morris J W, Lee C S, Guo Z. ISIJ Int, 2003; 43: 410
|
| [23] | Tomio Y, Furuhara T, Maki T. Mater Trans, 2009; 50: 2731
|
| [24] | Furuhara T, Takayama N, Miyamoto G. Mater Sci Forum, 2010; 638-642: 3044
|
| [25] | Koo J Y, Luton M J, Bangaru N V, Petkovic R A. Int J Offshore Polar Eng, 2004; 14: 75
|
| [26] | Li W W, Liu Y X, Gao H L, Zhao X W, Feng Y R, Ji L K. Trans China Weld Inst, 2006; 27: 43
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|