Al/有机硅涂层对304不锈钢在400℃盐和水蒸气综合作用下的防护作用
, PP. 301-303
Keywords: 不锈钢 ,NaCl ,水蒸气
Abstract:
研究了304不锈钢在400℃、盐和水蒸气综合作用下的腐蚀行为及添加Al粉的有机硅涂层对不锈钢的防护作用.结果表明，304不锈钢裸样发生了较为严重的腐蚀.刷涂了有机硅涂层的304不锈钢在相同的条件下没有发生腐蚀，涂层对304不锈钢具有优异的防护作用.讨论了有机硅涂层的防护机理.
References
[1] EEvans H E,Hilton D A,Holm RA,et al.The oxidation of astainless steel with limited quantities of sea salt[J].Oxid.Met.,1981,16(3/4):327. [2] MMisra R D K,Sivakumar R.Effect of NaCl vapor on the oxida-tion of Ni-Cr alloys[J].Oxid.Met.,1986,25(1/2):83. [3] YYao Z,Marek M.NaCl-induced hot corrosion of a titanium a-luminide alloy[J].Mat.Sci.Eng.,1995,A192/193:994. [4] WWang F,Shu Y.Influence of Cr content on the corrosion ofFe-Cr alloys:The synergistic effect of NaCl and water vapor[J].Oxid.Met.,2003,59(3/4):201. [5] BBourhis Y,John C St.Na2SO4-and NaCl-induced hot corrosionof six nickel-base superalloys.Oxid.Met.,1975,9(5/6):507. [6] KKofstad P.High temperature corrosion[M].Elsevier,Appl.Sci.,London,1988.382. [7] SShu Y,Wang F,Wu W.Synergistic effect of NaCl and watervapor on the corrosion of 1Cr-11Ni-2W-2Mo-V steel at 500℃~700℃[J].Oxid.Met.,1999,51(1/2):97. [8] SShu Y,Wang F,Wu W.Corrosion behavior of pure Cr with asolid NaCl deposit in O2plus water vapor[J].Oxid.Met.,2000,54,(5/6):457. [9] YYamauchi A,Kurokawa K,Takahashi H.Evaporation ofCr2O3in atmospheres containing H2O[J].Oxid Met.,2003,59(5/6):517. [10] Asteman H,Svensson J E,Norell M,et al.Influence of watervapor and flow rate on the high-temperature oxidation of304L:effect of chromium oxide hydroxide evaporation[J].Ox-id Met.,2000,54,(1/2):11. [11] Michihisa Fukumoto,Shigeru Maeda,Shigenari Hayashi,et al.Effect of water vapor on the oxidation behavior of Fe-1.5Si inair at 1073 and 1273 K[J].Oxid Met.,2001,55(5/6):401. [12] 周琳宁.有机硅聚合物导论[M].北京:科学出版社,2000.44. [13] 幸松民,王一璐.有机硅合成工艺及产品应用[M].北京:化学工业出版社,2000.744
Full-Text
Contact Us
service@oalib.com
QQ:3279437679
WhatsApp +8615387084133