Origen y endurecimiento por dispersión de carbonitruros en un acero comercial microaleado al niobio y laminado en caliente

Throughout this work, a study on niobium carbonitrides formation and its hardening effect in a commercial hot strip microalloyed steel is presented. Optic and electron micrographs were obtained while mechanical tests and indirect models allow to predict samples yield strength, taking into account the steel composition and its structural characteristics. The results showed an extended precipitation on austenite boundary cells during the last thermomechanical processing stages, which probably achieved a considerable contribution to the hardening by dispersion in the material studied. Otherwise, no evidence of precipitation in ferrite by means of transmission electron microscopy (TEM) was observed. A poor interphase precipitation was detected in about 10 per cent of the total observed zones with no appreciated contribution to the steel hardness. Se presenta un estudio sobre el origen de los carbonitruros de niobio y su efecto en el endurecimiento de un acero comercial microaleado y laminado en caliente. Para tal fin se utilizaron micrografías ópticas y electrónicas; así como también ensayos mecánicos y modelos indirectos que permitieron predecir el límite elástico teniendo en cuenta la composición del acero y sus características estructurales. Los resultados mostraron una extensa precipitación en la austenita durante las últimas fases del proceso de laminación siendo ésta responsable del principal aporte al endurecimiento por dispersión en el material investigado. No hubo evidencias de precipitación en la ferrita por observaciones al microscopio electrónico de transmisión y sólo una escasa precipitación interfásica fue detectada en un 10 % de las zonas observadas sin una apreciable contribución al endurecimiento del acero.