Structural characterization and ferroelectric properties of strontium barium niobate (SrxBa1-xNb2O6) thin films

Strontium barium niobate (SBN) thin films of good quality were deposited on Pt/Ti/SiO2/Si substrate using a polymeric resin containing metallic ions. Films were crystallized at different temperatures and for different duration of time. The structure of these films was studied using X-ray diffraction. The coexistence of SrNb2O6 (SN) and SBN was observed in films crystallized at 700 °C. The amount of SN decreases when the crystallization time increases. Ferroelectric properties were determined for films crystallized at 700 °C for 1 and 5 h. For SBN film crystallized at 700 °C for 1 h, the remanent polarization (Pr) and the coercive field (Ec) were 2.6 muC/cm2 and 71.9 kV/cm, respectively. For the film crystallized at 700 °C for 5 h these parameters were Pr = 1.1 muC/cm2 and Ec = 50.5 kV/cm.