Kinetics of Preparation of Ni Electroless Plating on ZrO2 Uultrafinepowders
ZrO2微粉表面化学镀镍动力学研究

In the process of electroless plating used to Ni coated ZrO2 ultrafine powders, the relationship between Ni2 concentration in solution and time at different temperatures was determined.The effect of Ni2 concentration, NaF and surfactants on the speed of Ni deposit was obtained.Apparent activity energy was concluded. The goal that even mixing Ni with ZrO2 was attained.Experimental results show that Ni is coated on ZrO2 powder surface and the speed of Ni deposit can be raised and apparent activity energy can be dropped by NaF and surfactants.