%T Determination of Some Mechanical Properties of Laminated Wood Material Reinforced with Carbon Fiber (CFRP)
%J -
%D 2018
%X In this study, it was aimed to determine the effect of some mechanical properties of structural laminated wood reinforced with carbon fiber. Laminated sheets were obtained using moisture curing polyurethane and two component epoxy adhesives prepared from Oriental beech (Fagus orientalis L.) wood samples. Carbon fiber (CFRP) structural material was applied to laminated sheets in order to increase their strength. Static bending test was made according to TS 2474, bending in elasticity modulus was made according to 2478, and dynamic bending (shock) test was made according to 2477 standards. According to results of the experiments, the highest static bending strength value (132.80 N/mm2) was obtained in laminated sheets used carbon fiber building material between wooden layers and bonded with epoxy adhesive. The highest elasticity modulus in bending value (14004.83 N/mm2) was determined in laminated sheets bonded with epoxy adhesive between wooden layers and covered with carbon fiber structural material around sheets. The highest dynamic bending (shock) strength value (0.62 kgm/cm2) was found in laminated sheets bonded with epoxy adhesive between wooden layers and covered with carbon fiber structural material around sheets. Consequently, carbon fiber building material and epoxy adhesive can be used in sections which are exposed to bending and stress such as bridge, stair, column, beam, and roof for local reinforcement. Damage of wood material can be prevented by using carbon fiber construction material and epoxy adhesive against the sudden effects that might be caused to the outside of the wood material. Due to the strong and fast penetration of the epoxy adhesive on the applied surface and the increased strength with the carbon fiber building material, it can be used to extend the wear time especially on the floors made of wood
%K Lamine A£¿a£¿ Malzeme
%K Karbon Fiber (CFRP)
%K Yap£¿£¿t£¿r£¿c£¿lar
%K Mekanik £¿zellikler
%U http://dergipark.org.tr/mbd/issue/40281/441729