%0 Journal Article
%T Kinetic Model of LiFePO4 Formation Using Non-Isothermal Thermogravimetric Analysis
%A Abdul Halim
%A Heru Setyawan
%A Sugeng Winardi
%A Widiyatuti Widiyastuti
%J -
%D 2014
%R 10.9767/bcrec.9.1.5508.60-65
%X The formation reaction of LiFePO4 from decomposition of precursors LiOH, FeSO4.7H2O and (NH4)2HPO4 with mol ratio of Li:Fe:P=1:1:1 was investigated. The experiment was carried out by thermogravimetric differential thermal analysis (TG-DTA) method using nitrogen as atmosfer at a constant heating rate to obtain kinetic constant parameters. Several heating rates were selected, there are 5, 7, 10, 15, 17.5, 22.5 and 25 ¡ãC/min. Activation energy, pre-exponential factor and reaction order were taken using Kissinger method and obtained respectively 56.086 kJ/mol, 6.95¡Á108 min-1, and 1.058. Based on fitting result between reaction model and experiment were obtained that reaction obeyed the three dimension diffusion model. £¿ 2014 BCREC UNDIP. All rights reserved Received: 19th September 2013; Revised: 9th December 2013; Accepted: 23rd January 2014 [How to Cite: Halim, A., Widiyastuti, W., Setyawan, H., Winardi, S. (2014). Kinetic of LiFePO4 For-mation Using Non-isothermal Thermogravimetric Analysis. Bulletin of Chemical Reaction Engineering & Catalysis, 9 (1): 60-65. (doi:10.9767/bcrec.9.1.5508.60-65)] [Permalink/DOI: http://dx.doi.org/10.9767/bcrec.9.1.5508.60-65
%K LiFePO4
%K Thermogravimetric Differential Thermal Analysis
%K Kinetics Reaction
%U https://ejournal.undip.ac.id/index.php/bcrec/article/view/5508