%X 通过正交试验优化预聚体各组分配比和调整阻燃剂、抑烟剂和成炭剂的用量合成聚氨酯（PU）弹性体，并对其物理性能和燃烧性能进行研究。结果表明：优化配方制备的PU弹性体拉伸强度达3.99 MPa.拉断伸长率达800%．具有良好的成炭性和显著的绝热效果，极限氧指数达37.4%，线烧蚀速率为0.35 mm·s<sup>-l</sup>，且在燃烧时低烟、微烟甚至几乎达到无烟。;ln this study， polyurethane elastomer （PU） was prepared by using orthogonal experimental design to optimize the ratio of prepolymer components， the addition levels of flame retardant ，smokesuppression agent and charring agent. The physical properties and combustion performance of the PU elastomer were investigated. The results showed that ， the tensile strength of the optimized PU elastomer reached 3.99  MPa ， and the elongation at break was 800% . It possessed good charring effect and remarkable heat insulating effect. The limiting oxygen index reached 37.4% ，the ablation rate was0.35 mm·s<sup>-l</sup> ，and in the combustion test， the elastomer showed very little smoke or even no smoke
%K [聚氨酯弹性体
%K 合成
%K 微烟
%K 物理性能
%K 燃烧性能
%K 正交试验设计
%K 聚氨酯弹性体
%K 合成
%K 微烟
%K 物理性能
%K 燃烧性能
%K 正交试验设计
%K polyurethane elastomer
%K synthesis
%K low  smoke
%K physical  property
%K combustion  performance
%K orthogonal experimental design]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20150106&flag=1