%0 Journal Article
%T 镀镍石墨/硅橡胶导电复合材料的性能研究
%A 张立群
%A 田明
%A 谢丽丽
%A 赵素合
%A 邹华
%J -
%D 2008
%X 以镀镍石墨为导电填料制备镀镍石墨/甲基乙烯基硅橡胶（MVQ）导电复合材料，并对其性能进行研究。结果表明，采用密炼工艺、硫化温度为110 ℃、偶联剂A-151和硫化剂双24用量分别为6和8份时，所制备的镀镍石墨/MVQ复合材料的导电性能和拉伸性能较好。;A nickel-coated graphite/silicone rubber electrical conductive composite was prepared，and its properties were investigated.The results showed that the composite filled with 6 phr coupling agent A-151 and 8 phr curing agent DCBP，blended using internal mixer and vulcanized at 110 ℃ possessed better electrical conductivity and tensile strength
%K [镀镍石墨
%K 硅橡胶
%K 复合材料
%K 导电性能
%K 镀镍石墨
%K 硅橡胶
%K 复合材料
%K 导电性能
%K nickel-coated graphite
%K silicone rubber
%K composite
%K electrical conductivity]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20080204&flag=1