%T 溴化对-特辛基酚醛硫化树脂对IIR动态力学性能的影响
%A 李超芹
%A 王永刚
%J -
%D 2011
%X 研究溴化对-特辛基酚醛硫化树脂(201树脂）对IIR动态力学性能的影响。结果表明：随着201树脂用量的增大，IIR硫化胶的损耗峰明显向高温方向移动，最大损耗因子呈减小趋势；在较低温度下，IIR硫化胶的储能模量（E′）随201树脂用量的增大逐渐减小；在较高温度下，IIR硫化胶的E′随201树脂用量的增大逐渐增大，损耗模量降低的平台逐渐升高。;The effect of brominated p-tert-octyl phenolic-formadehyde curing resin(201 resin) on the dynamic mechanical properties of IIR was investigated.The results showed that,as the addition level of 201 resin increased,the tanδ peaks of IIR vulcanizates shifted to higher temperature zone,and the maximum value of tanδ tended to decrease;at low temperature,the storage modulus（E′） of IIR vulcanizate decreased gradually;however,at high temperature range,theE′increased gradually,and the platform of loss modulus elevated gradually
%K [IIR
%K 溴化对-特辛基酚醛硫化树脂
%K 动态力学性能
%K IIR
%K 溴化对-特辛基酚醛硫化树脂
%K 动态力学性能
%K IIR
%K brominated p-tert-octyl phenolic-formadehyde curing resin
%K dynamic mechanical property]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20110204&flag=1