%0 Journal Article
%T 氯化丁基橡胶/丁腈橡胶宽温域阻尼材料的制备及性能研究
%A 冯翰林
%A 曾宪奎
%A 焦淑莉
%A 高远昊
%A 鲍丽苹
%J -
%D 2019
%R 10.12136/j.issn.1000-890X.2019.01.0018
%X 制备氯化丁基橡胶（CIIR）/丁腈橡胶（NBR）宽温域阻尼材料，研究CIIR/NBR并用比以及765树脂、木质纤维素和石墨烯的用量对并用胶阻尼性能的影响。结果表明：当CIIR/NBR并用比为30/70，765树脂、木质纤维素和石墨烯的用量分别为4，10和5份时，并用胶具有较宽的阻尼温域。;The CIIR/NBR damping material for wide temperature range application was prepared，and the effects of CIIR/NBR blending ratio，the amount of 765 resin，lignocellulose and graphene on the damping properties of the blends were investigated. The results showed that，when the CIIR/NBR blending ratio was 30/70，and the amounts of 765 resin，lignocellulose and graphene were 4，10 and 5 phr，respectively，the blends had a wide damping temperature range
%K [氯化丁基橡胶
%K 丁腈橡胶
%K 并用胶
%K 树脂
%K 木质纤维素
%K 石墨烯
%K 阻尼温域
%K 氯化丁基橡胶
%K 丁腈橡胶
%K 并用胶
%K 树脂
%K 木质纤维素
%K 石墨烯
%K 阻尼温域
%K CIIR
%K NBR
%K blend
%K resin
%K lignocellulose
%K graphene
%K damping temperature range]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ2017-0295&flag=1