%T 硅树脂对双组分室温硫化硅橡胶耐热性能的影响
%A 姜威
%A 方庆红
%A 杨凤
%A 王娜
%A 赵妍
%J -
%D 2014
%X 研究硅树脂用量对双组分室温硫化硅橡胶耐热性能的影响。结果表明：随着硅树脂用量的增大，硅橡胶的邵尔A型硬度、拉伸强度和拉断伸长率呈增大趋势，耐热性能先提高后降低；当硅树脂用量为8份时，硅橡胶的拉伸性能和耐老化性能最佳；当硅树脂用量为6份时，硅橡胶的耐热性能最佳。;The effect of addition level of silicone resin on the heat resistance of two-component room temperature vulcanized silicone rubber was investigated.The results showed that，as the addition level of silicone resin increased，the Shore A hardness，tensile strength and elongation at break of silicone rubber tended to increase，and the heat resistance increased at first and then decreased.When the addition level of silicone resin was 8 phr，the best tensile property and aging property of silicone rubber were obtained.When the addition level of silicone resin was 6 phr，the best heat resistance of silicone rubber was achieved
%K [双组分室温硫化硅橡胶
%K 硅树脂
%K 耐热性能
%K 耐老化性能
%K 热重分析
%K 双组分室温硫化硅橡胶
%K 硅树脂
%K 耐热性能
%K 耐老化性能
%K 热重分析
%K two-component room temperature vulcanized silicone rubber
%K silicone resin
%K heat resis-tance
%K aging property
%K thermogravimetric analysis]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20140602&flag=1