%T 耐高温耐老化龟裂氟橡胶/三元乙丙橡胶并用胶的制备与性能研究
%A 包志方
%A 孙业斌
%A 张立群
%A 李剑
%A 田明
%J -
%D 2015
%X 研究硫化体系、氟橡胶（FKM）/三元乙丙橡胶（EPDM）并用比、相容剂马来酸酐接枝三元乙丙橡胶（MA-g-EPDM）对FKM/EPDM并用胶物理性能以及耐高温和耐老化龟裂性能的影响。结果表明：随着硫化剂DCP用量的增大，FKM/EPDM并用胶的邵尔A型硬度和拉伸强度提高，拉断伸长率降低；随着FKM/EPDM并用比的增大，FKM/EPDM并用胶的拉伸强度和拉断伸长率均降低，但耐老化龟裂性能提高；FKM/EPDM并用比为30/70、硫化剂DCP用量为3份时，FKM/EPDM并用胶具有较好的综合性能；添加相容剂MA-g-EPDM不能提高FKM/EPDM并用胶的物理性能。;The effects of curing system，FKM/EPDM ratio and compatibilizer maleic anhydride grafted EPDM（MA-g-EPDM）on the physical properties，high-temperature resistance and long term cracking resistance of FKM/EPDM blend were investigated. The results showed that，when the addition level of curing agent DCP increased，the Shore A hardness and tensile strength of FKM/EPDM blend increased，but the elongation at break decreased. When the ratio of FKM/EPDM increased，the tensile strength and elongation at break of FKM/EPDM blend decreased，but the cracking resistance under aging was improved.When the addition level of curing agent DCP was 3 phr，and ratio of FKM/EPDM was 30/70，the FKM/EPDM blend had good properties. There was no effect on the improvement of physical properties of FKM/EPDM when MA-g-EPDM was used
%K [氟橡胶
%K 三元乙丙橡胶
%K 并用胶
%K 耐高温性能
%K 耐老化龟裂性能
%K 氟橡胶
%K 三元乙丙橡胶
%K 并用胶
%K 耐高温性能
%K 耐老化龟裂性能
%K FKM
%K EPDM
%K blend
%K high-temperature resistance
%K long term cracking resistance]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=xj20151102&flag=1