%T 芳纶纤维与表面处理层界面粘合机理研究
%A 夏涛
%A 申明霞
%A 蒋林华
%A 费传军
%A 邓洪
%J -
%D 2007
%X 用扫描电子显微镜（SEM）和电子能谱仪（XPS）研究芳纶纤维与表面处理层界面粘合机理。结果表明，采用封闭异氰酸酯以及RFL胶乳体系浸渍处理后的芳纶纤维表面增加了一种新的结合碳，而且其它碳的结合能向高能方向移动，纤维表面处理层的氮原子所占比例增大，提高了芳纶纤维的表面活性。;The adhesion mechanism of aramid fibre/coating interface was investigated by scanning electron microscope and X-ray photoelectron spectroscopy.The results showed that a new combined carbon appeared on the surface of aramid fibre when it was treated with blocked isocyanate and resorcinol-formaldehyde-latex，and the binding energy of the other combined carbon shifted to a higher value，the proportion of nitrogen increased，and the surface activity of aramid fibre was improved