%T 在同步带硫化过程中浸胶玻璃纤维线绳强力损失的原因分析
%A 于得江
%A 姜伟
%A 姜华
%A 高渭淞
%J -
%D 2020
%R 10.12136/j.issn.1000-890X.2020.01.0069
%X 分析浸胶玻璃纤维线绳在同步带硫化过程中强力损失的原因。试验结果表明：浸胶玻璃纤维线绳在以氯丁橡胶（CR）为主体材料的硫化过程中强力损失较大，CR胶料硫化过程中产生的水和盐酸均会对浸胶玻璃纤维线绳的强力产生影响，且随着温度升高，影响愈加明显。;The reason of strength loss of dipped glass fiber rope during the vulcanization of synchronous belt was analyzed.The test results showed that the strength loss of the dipped glass fiber rope was larger during the vulcanization in the CR compound.The water and hydrochloric acid produced during the CR compound vulcanization had effected on strength of dipped glass fiber rope，and the effect was stronger as the temperature was higher
%K [浸胶玻璃纤维线绳
%K 同步带
%K 氯丁橡胶
%K 强力损失
%K 硫化
%K 浸胶玻璃纤维线绳
%K 同步带
%K 氯丁橡胶
%K 强力损失
%K 硫化
%K dipped glass fiber rope
%K synchronous belt
%K CR
%K strength loss
%K vulcanization]