%0 Journal Article
%T 聚苯胺/NBR复合材料的制备与性能研究
%A 吴其晔
%A 范海军
%A 陈骁
%J -
%D 2008
%X 分别采用溶液法和乳液法合成盐酸和十二烷基苯磺酸掺杂的聚苯胺（PANI），研究PANI/NBR复合材料的硫化特性、导电性能和物理性能。结果表明，随着PANI用量的增大，复合材料的M<sub>H</sub>增大，t<sub>10</sub>和t<sub>90</sub>先延长后缩短；掺杂态PANI用量对复合材料的电导率影响较小；随着PANI用量的增大，复合材料的拉伸强度、邵尔A型硬度和100％定伸应力明显增大，拉断伸长率先增大后减小，在PANI为30份时达到最大值。;Polyaniline（PANI） doped with HCl and dodecylbenzenesulfonic acid were synthesized by solution polymerization and emulsion polymerization respectively，and the vulcanization characteristics，conductivity and physical properties of PANI/NBR composite were investigated.The results showed that the M<sub>H</sub> of the composite increased，t<sub>10</sub> and t<sub>90</sub> increased at first and then decreased as the addition level of PANI increased；the conductivity of the composite were influenced only a little by PANI；with the increase of the addition level of PANI，the tensile strength，Shore A hardness and modulus at 100% elongation of the composite increased significantly，and the elongation at break increased at first，reached the maximum value as the addition level of PANI was 30 phr，and then decreased
%K [聚苯胺
%K NBR
%K 复合材料
%K 电导率
%K 物理性能
%K 聚苯胺
%K NBR
%K 复合材料
%K 电导率
%K 物理性能
%K PANI
%K NBR
%K composite
%K conductivity
%K physical properties]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20081003&flag=1