%0 Journal Article
%T 三元乙丙橡胶与未处理聚酯帆布的粘合性能研究
%A 刘维
%A 吴建国
%A 孙业斌
%A 田明
%A 萨日娜
%A 顾征宇
%J -
%D 2015
%X 研究过氧化二异丙苯（DCP）和马来酰亚胺类物质（M）对三元乙丙橡胶（EPDM）与末处理聚酯帆布粘合性能的影响。结果表明：采用DCP为引发剂、M为交联剂的硫化体系所制备的EPDM硫化胶具有较好的物理性能，在常温和200 ℃下与末处理聚酯帆布的粘合强度较高；当DCP/M用量比为0.75/3时，硫化胶的高温粘合强度达到耐热输送带的T3等级。;The effect of dicumyl peroxide（DCP）and maleic imide containing additive M on the adhesionproperty of EPDM and untreated polyester canvas was investigated.The results showed that，EPDM vulcanizate prepared with DCP as initiator and M as crosslinking agent had good physical properties，and the adhesion strength with untreated polyester canvas was high at room temperature and 200 ℃.It was found that when the blend ratio of DCP/M was 0.75/3，the adhesion strength of the vulcanizates at high temperature reached T3 level of heat resistantconveyor belt
%K [三元乙丙橡胶
%K 硫化体系
%K 聚酯帆布
%K 粘合性能
%K 三元乙丙橡胶
%K 硫化体系
%K 聚酯帆布
%K 粘合性能
%K EPDM
%K curing system
%K polyester canvas
%K adhesion property]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=xj20151204&flag=1