%0 Journal Article
%T 超细全硫化粉末丁苯橡胶/纳米碳酸钙复合粉末对丁苯橡胶性能的影响
%A 宋庆梅
%A 宋志海
%A 张晓红
%A 王庆国
%A 王琮
%J -
%D 2012
%X 采用超细全硫化粉末丁苯橡胶（UFPSBR）/纳米碳酸钙复合粉末制备UFPSBR/纳米碳酸钙/丁苯橡胶（SBR）纳米复合材料，并对其性能进行研究。结果表明：随着UFPSBR/纳米碳酸钙复合粉末用量的增大，UFPSBR/纳米碳酸钙/SBR纳米复合材料的硫化时间缩短、硫化速率加快、物理性能和阻燃性能提高，同时玻璃化温度下降、储能模量增大。;The ultrafine fully vulcanized powder SBR （UFPSBR）/nano-calcium carbonate （nano-CaCO<sub>3</sub>）/SBR nano-composites were prepared by UFPSBR/nano-CaCO<sub>3</sub> compounded powder，and the properties of composites were investigated.The results showed that，as the addition level of UFPSBR/nano-CaCO<sub>3</sub> compounded powder increased，the curing time of UFPSBR/nano-CaCO<sub>3</sub>/SBR nano-composites was shortened，curing speed was accelerated，physical properties and flame retardant property were improved，glass transition temperature was decreased，and storage modulus was increased
%K [超细全硫化粉末橡胶
%K 纳米碳酸钙
%K 丁苯橡胶
%K 动态力学性能
%K 阻燃性能
%K 超细全硫化粉末橡胶
%K 纳米碳酸钙
%K 丁苯橡胶
%K 动态力学性能
%K 阻燃性能
%K ultrafine fully vulcanized powder rubber
%K nano-calcium carbonate
%K SBR
%K dynamic mechanical property
%K flame retardant property]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20120902&flag=1