%T 动态硫化CR/PVC热塑性弹性体的性能
%A 吴明生
%A 孟宪德
%A 张国年
%A 杜爱华
%A 纪奎江
%J -
%D 2001
%X 以CR胶乳和PVC 乳液共沉物为原料，通过动态硫化法制成CR/PVC热塑性弹性体。研究了混炼温度和橡塑共混比对CR/PVC共混物力学性能的影响，并通过电镜观察CR/PVC共混物的微观结构。结果表明，在(165±10) ℃下制得的CR/PVC共混物的综合性能较好；动态硫化CR/PVC 共混物比静态硫化CR/PVC共混物具有更好的力学性能。;The dynamically cured CR/PVC thermoplastic elastomer was prepared with CR latex/PVC emulsion codeposite.The influence of the mixing temperature and blending ratio on the mechanical properties of CR/PVC blend was investigated and the microstructure of CR/PVC blend was observed on TEM.The results showed that the CR/PVC blend mixed at (165±10) ℃ had better comprehensive properties；the dynamically cured CR/PVC blend had better mechanical properties when compared with the statically cured CR/PVC blend
%K [CR
%K PVC
%K 动态硫化
%K 热塑性弹性体
%K CR
%K PVC
%K 动态硫化
%K 热塑性弹性体
%K CR
%K PVC
%K dynamic vulcanization
%K thermoplastic elastomer]