%T 溶液法丁基橡胶硫化胶囊的研制
%A 刘志琴
%A 刘秀兰
%A 潘广勤
%A 焦宏宇
%A 胡开放
%A 苟发荣
%J -
%D 2013
%X 分别以淤浆法和溶液法丁基橡胶（IIR）制备全钢载重子午线轮胎硫化胶囊，并对其性能进行对比研究。结果表明：采用硫化胶囊标准配方，淤浆法IIR硫化胶的物理性能较好，溶液法IIR硫化胶的耐热老化性能较好且硫化时间较短；采用硫化胶囊生产配方，溶液法与淤浆法IIR硫化胶物理性能相差不大，溶液法IIR硫化胶的耐热老化性能较好。两种IIR硫化胶囊质量相当，均达到了工厂使用要求。;The truck and bus radial tire curing bladders were prepared by using slurry and solution IIR respectively，and their properties were investigated.The results showed that， when standard formula was used，the physical property of slurry IIR vulcanizates was better，the optimium cure time of solution IIR was shorter，and the heat aging property of solution IIR vulcanizates was better.When production formula was used， the physical property was similar，and the heat aging property of solution IIR vulcanizates was better.The qualities of these two IIR based curing bladders were similar，and both of them met the operational requirement for factory
%K [溶液法
%K 淤浆法
%K 丁基橡胶
%K 硫化胶囊
%K 溶液法
%K 淤浆法
%K 丁基橡胶
%K 硫化胶囊
%K solution method
%K slurry method
%K IIR
%K curing bladder]
%U http://www.rubbertire.cn/gy/xjgy/ch/reader/view_abstract.aspx?file_no=XJ20131008&flag=1