%0 Journal Article
%T Improvement in Wear Resistance of AISI H13 Steel by Pack-Boronizing Method
%A Akshay Joshi
%A Niketan Manthani
%A Rajkumar Singh
%A Vinayak Pawar
%J -
%D 2018
%X Boronizing has been employed to increase the service life   of parts such as orifices, ingot molds and dies for hot   forming made of AISI H13steel. In this study, pack   boronizing was done of AISI H13 Steel. Samples were   boronized at 950ˇăC for 0.5 hr, 1 hr and 4 hr. In all the   specimens both the iron boride layers (FeB, Fe2B) were   formed. It was seen that as soaking time increases,   thickness of boride depth also increases. Continuous   decrease in the hardness from surface to unboronized   layer was observed. Boronized specimen at 950ˇăC for 4 hr   showed better hardness and so was studied for further   investigation. This study was compared with   Nitrocarburized cycle at 550ˇăC for 12 hr. High wear   resistance was observed in the boronized specimen than   in nitrocarburized sample. COF was ranging from 0.40 to   0.70.
%K Nanotechnology Research
%K list of open access journals
%K open access
%K open access journals
%K open access publication
%K open access publisher
%K open access publishing
%K open access journal articles
%K imedpub
%K imedpub publishing
%K insight medical publishing
%K imedpub online
%U https://www.imedpub.com/articles/improvement-in-wear-resistance-of-aisi-h13-steel-by-packboronizing-method.php?aid=22364