%0 Journal Article %T Structure and Electrical Properties of Na0.5Bi0.5TiO3 Epitaxial Films with (110) Orientation %J Crystals | An Open Access Journal from MDPI %D 2019 %R https://doi.org/10.3390/cryst9110558 %X Pt/Na 0.5Bi 0.5TiO 3/La 0.5Sr 0.5CoO 3 (Pt/NBT/LSCO) ferroelectric capacitors were fabricated on (110) SrTiO 3 substrate. Both NBT and LSCO films were epitaxially grown on the (110) SrTiO 3 substrate. It was found that the leakage current density of the Pt/NBT/LSCO capacitor is favorable to ohmic conduction behavior when the applied electric fields are lower than 60 kV/cm, and bulk-limited space charge-limited conduction takes place when the applied electric fields are higher than 60 kV/cm. The Pt/NBT/LSCO capacitor possesses good fatigue resistance and retention, as well as ferroelectric properties with P r = 35 ¦ÌC/cm 2. The ferroelectric properties of the Pt/NBT/LSCO capacitor can be modulated by ultraviolet light. The effective polarization, ¦¤P, was reduced and the maximum polarization P max was increased for the Pt/NBT/LSCO capacitor when under ultraviolet light, which can be attributed to the increased leakage current density and non-reversible polarization P^ caused by the photo-generated carriers. View Full-Tex %U https://www.mdpi.com/2073-4352/9/11/558