%0 Journal Article
%T 氧化石墨烯/有机改性膨润土复合材料的制备及其对Cd(Ⅱ)的吸附<br>Preparation of graphene oxide/organo-modified bentonite composites and their adsorption on Cd(Ⅱ)
%A 唐振平
%A 毕玉玺
%A 刘迎九
%A 滑熠龙
%A 凌辉
%A 谢水波
%J 复合材料学报
%D 2018
%R 10.13801/j.cnki.fhclxb.20180310.002
%X 以氧化石墨烯（GO）、膨润土（Bent）、十六烷基三甲基溴化铵（CTAB）为原料，合成了GO/有机改性Bent （OM-Bent）复合材料，用其处理浓度为10 mg·L-1的含Cd （Ⅱ）废水。研究了GO/OM-Bent复合材料中GO含量、pH、GO/OM-Bent复合材料投加量、反应时间、Cd （Ⅱ）初始浓度及共存离子对GO/OM-Bent复合材料吸附Cd （Ⅱ）的影响。结果表明：在pH值为6、GO质量分数为30wt%、GO/OM-Bent复合材料投加量为200 mg·L-1时，GO/OM-Bent复合材料吸附Cd （Ⅱ）效果最佳，120 min即达到平衡，较同等条件下OM-Bent和GO单独作用时Cd （Ⅱ）吸附量分别高12.01 mg·g-1和5.39 mg·g-1；准二级动力学模型能很好地描述其吸附过程，吸附等温线符合Langmuir模型，温度为303 K时，GO/OM-Bent复合材料对Cd （Ⅱ）的最大吸附量为133.33 mg·g-1。解吸实验结果表明，经5次吸附-解吸循环实验后，Cd （Ⅱ）的吸附率仍高达83.5%，说明GO/OM-Bent复合材料具有很好的循环再生性能。 Graphene oxide/organo-modified bentonite(GO/OM-Bent) composites were prepared by the synthesis of GO, Bent and cetyltrimethyl ammonium bromide (CTAB), then the composites were used to treat Cd(Ⅱ)-containing wastewater at a concentration of 10 mg·L-1. The effects of GO content in GO/OM-Bent composite, pH value, GO/OM-Bent composite dosage, reaction time, initial concentration of cadmium and coexisting ions on adsorption of Cd(Ⅱ) by GO/OM-Bent composite were investigated by batch test. The adsorption results of GO/OM-Bent composites are balanced at 120 min with the best effect on Cd(Ⅱ) adsorption under the optimal condition:the pH value is 6, the mass fraction of GO is 30wt%, the GO/OM-Bent composite dosage is 200 mg·L-1; Under the same conditions, the adsorption capacity of GO/OM-Bent composite is 12.01 mg·g-1 and 5.39 mg·g-1 higher than that of OM-Bent and GO, respectively; the pseudo-second-order kinetics model can well describe the adsorption process and the adsorption isotherm conforms to the Langmuir model. At 303 K, the maximum adsorption capacity of GO/OM-Bent composite on Cd(Ⅱ) could be reached 133.33 mg·g-1. The results of desorption test shows that the adsorption efficiency of Cd(Ⅱ) remains as high as 83.5% after 5 cycles of adsorption-desorption, indicating that GO/OM-Bent composite has good cyclic regeneration performance. 湖南省自然科学基金（2016JJ6125）；国家自然科学基金（11475080）；湖南省教育厅（15C1192）
%K 氧化石墨烯
%K 有机改性膨润土
%K 吸附
%K 解吸
%K Cd (Ⅱ)
%K 共存离子&lt
%K br&gt
%K graphene oxide
%K organo-modified bentonite
%K adsorption
%K desorption
%K Cd (Ⅱ)
%K coexisting ion
%U http://fhclxb.buaa.edu.cn/CN/abstract/abstract14276.shtml