%0 Journal Article %T Ag-TiO<sub>2</sub>-MnO<sub>2</sub>复合材料的制备与电化学性能研究<br>Preparation and Electrochemical Performance of Ag-TiO<sub>2</sub>-MnO<sub>2 </sub>Composites %A 张伶潇 %A 赵惠慧 %A 张丽娟 %A 付予< %A br> %A ZHANG Ling-xiao %A ZHAO Hui-hui %A ZHANG Li-juan %A FU Yu %J 电化学 %D 2018 %R 10.13208/j.electrochem.171130 %X 摘要 采用高温固相法制备了Ag-TiO2共修饰的二氧化锰锂电池阴极材料，通过X射线衍射仪（XRD）、扫描电子显微镜（SEM）、傅立叶红外光谱仪（FT-IR）、X射线光电子能谱仪（XPS）、能量散射X射线能谱（EDS）、循环伏安测试（CV）、恒流放电测试、交流阻抗测试（EIS）等分别检测了所制备样品的物理-化学特性及相应的电化学性能特征.结果表明：空白二氧化锰与修饰后二氧化锰均为β 晶型，相比于未修饰样品，Ag-TiO2-MnO2 样品的形貌得到了明显的改变.修饰后样品大倍率的放电比容量显著提升，1C 下的容量由 75mAh·g-1 增加到 115mAh·g-1，Ag-TiO2-MnO2 样品 Mn-O 键能的增强对于抑制放电过程中体积膨胀也有一定作用，可以使二氧化锰材料保持较好的结构稳定性.<br>The silver-titanium dioxide co-modified manganese dioxide (Ag-TiO2-MnO2) cathode material was prepared through high temperature solid state reaction. The microstructure, phase composition and electrochemical performance of the prepared samples were characterized by X-ray diffraction spectroscopy (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectrometry (FT-IR), X-ray photoelectron spectroscopy (XPS), Energy-dispersive X-ray spectroscopy (EDS), Cyclic voltammetry (CV), galvanostatic discharge and electrochemical impedance spectroscopy (EIS). Results showed that the unmodified and Ag-TiO2 modified MnO2 samples both exhibited β-MnO2 structurebut with different morphologies. The EDS mapping results revealed that Ag was uniformly dispersed on the surface of manganese dioxide, while Ti was relatively non-uniform in the Ag-TiO2-MnO2 sample. The modified samples were effective in improving specific discharge capacities. The specific discharge capacity increased from 75 mAh·g-1 to 115 mAh·g-1 at the rate of 1C. The stronger bond energy of Mn-O in the modified MnO2 could suppress the volume expansion during the discharge process, which can maintain the structural stability of the manganese dioxide material %K 二氧化锰阴极材料 %K Ag-TiO< %K sub> %K 2< %K /sub> %K 修饰 %K 电化学性能 %K < %K br> %K < %K p class= %U http://electrochem.xmu.edu.cn/CN/abstract/abstract10445.shtml