%T 硅铝比对无碱铝硼硅酸盐玻璃高温粘度 和析晶性能的影响<br>Effect of the Ratio of SiO2 and Al2O3 on the Viscosity and Crystallization of Non-Alkali Aluminoborosilicate Glasses at High Temperature
%A 田中青
%A 朱昱恺
%A 黄伟九
%A 杜迅
%A 李喜林
%J Hans Journal of Chemical Engineering and Technology
%P 82-85
%@ 2161-8852
%D 2013
%I Hans Publishing
%R 10.12677/HJCET.2013.33015
%X 研究了硅铝比对无碱铝硼硅酸盐玻璃高温粘度和析晶性能的影响。结果表明，随着硅铝比的增加，无碱铝硼硅酸盐系统玻璃的高温粘度、成型温度和粘滞活化能增加，液相温度降低，成型温度与液相线温度的差值增大。<br />
Effect of the ratio of SiO2 and Al2O3 on the viscosity and crystallization of non-alkali aluminoborosilicate glasses at high temperature was investigated. The results showed that the viscosity, the fiber-drawing temperature and the activation energy for vicious flow were increased, the liquidus temperature was decreased and the difference between the fiber-drawing temperature &amp; the liquidus temperature was increased with the ratio of SiO2 and Al2O3 increased.
%K 粘度；成型温度；析晶<br>Viscosity
%K Fiber-Drawing Temperature