%0 Journal Article
%T Produ  o de fibras de hidroxiapatite por electrofia  o
%A P. Q. Franco
%A J.C. Silva
%A J.P. Borges
%J Ci¨ºncia & Tecnologia dos Materiais
%D 2010
%I Scientific Electronic Library Online
%X Neste trabalho desenvolveu-se um novo m¨¦todo de produ  o fibras de hidroxiapatite (HA), combinando a t¨¦cnica de electrofia  o com um sistema sol-gel de base n o-alc¨®xida, utilizando precursores baratos. Como precursores de f¨®sforo e de c¨¢lcio, foram usados o pent¨®xido de f¨®sforo (P2O5) e o nitrato de c¨¢lcio tetrahidratado (Ca(NO3)2.4H2O), respectivamente. As fibras obtidas resultam da electrofia  o de uma mistura do gel formado a partir do sistema Ca(NO3)2.4H2O/P2O5 com solu  es polim¨¦ricas de polivinilpirrolidona (PVP) em ¨¢gua e misturas etanol/¨¢gua. As fibras obtidas foram analisadas quanto ¨¤ sua morfologia (Microscopia Electr¨®nica de Varrimento, MEV), composi  o qu¨ªmica (Espectroscopia de Infravermelho de transformada de Fourier, FTIR) e estrutural (Difrac  o de raios-X, DRX). Obtiveram-se nano e microfibras, maioritariamente constitu¨ªdas por HA carbonatada do tipo B e com vest¨ªgios de ¨®xido de c¨¢lcio (CaO) e de ¦Â-fosfato tric¨¢lcico (¦Â-TCP). Pela an¨¢lise de MEV verificou-se que uma maior concentra  o de PVP nas solu  es de electrofia  o conduz ¨¤ forma  o de fibras de forma cil¨ªndrica e que uma maior quantidade de ¨¢gua permite obter fibras de menor diametro e com menor dispers o de diametros. As fibras de HA produzidas t¨ºm potencial para a utiliza  o quer biotecnol¨®gica (por ex. membranas de permuta i¨®nica), quer biom¨¦dica (por ex. matrizes para crescimento de c¨¦lulas ¨®sseas). This paper reports a new method of producing hydroxyapatite (HA) fibres, combining electrospinning and a non-alcoxide sol-gel system, using cheap precursors. Phosphorus pentoxide (P2O5) and calcium nitrate tetrahydrate (Ca(NO3)2.4H2O) were used as precursors of phosphorus and calcium, respectively. The fibres were electrospun from a mixture of the gel formed from the system Ca(NO3)2.4H2O/P2O5 with polymeric solutions of polyvinylpyrrolidone (PVP) in water and ethanol/water mixtures. The fibres were analyzed for their morphology (Scanning Electron Microscopy, SEM), chemical composition (Fourier Transform Infrared Spectroscopy, FTIR) and structure (X-ray diffraction, XRD). Nano and microfibres were obtained, composed mainly of type B carbonated HA with traces of calcium oxide (CaO) and ¦Â-tricalcium phosphate (¦Â-TCP). From SEM analysis it was found that higher concentration of PVP in the electrospinning solutions leads to the formation of cylindrical fibres and that a larger amount of water allows for smaller diameter fibres and narrow diameters distribution. HA fibres produced have potential use either in Biotechnology (eg. Ion-exchange membranes) and Biomedicine (eg. Scaffolds fo
%K Hidroxiapatite
%K Sol-gel
%K Electrofia  o
%K Microfibras
%K Nanofibras
%K Hydroxyapatite
%K Sol-gel
%K Electrospinning
%K Microfibres
%K Nanofibres
%U http://www.scielo.oces.mctes.pt/scielo.php?script=sci_arttext&pid=S0870-83122010000100006