%0 Journal Article %T Five Layers Aurivillius Phases Pb2-xBi4+xTi5-xMnxO18: Synthesis, Structure, Relaxor Ferroelectric and Magnetic Properties %A Zulhadjri %A B. Prijamboedi %A A.A. Nugroho %A N. Mufti %J ITB Journal of Science %D 2011 %I %X Synthesis of five layers Aurivillius phases, Pb2-xBi4+xTi5-xMnxO18 (0 ¡ê x ¡ê 1) were carried out by molten salts method using eutectic mixture of Na2SO4/K2SO4 salts (1:1 molar ratio) as the flux. The samples were characterized by X-ray diffraction powder and refined by Le Bail technique. The refinement results revealed that the samples with composition x = 0, 0.2, 0.4, and 0.6 formed five layers Aurivillius with the space group B2cb; however, the samples with x = 0.4 and 0.6 contained impurity as BiMnO3 and the additional phase of four layers Aurivillius (PbBi4Ti4O15) was also observed for x = 0.6. The samples with x = 0.8 and 1 resulted in two phases: four layers Aurivillius and BiMnO3. The dielectric properties of the Pb2-xBi4+xTi5-xMnxO18 show broad peaks with anomaly (Tm) at temperature 295 ¡ãC, 295 ¡ãC, 304 ¡ãC, and 343 ¡ãC at frequency 2 MHz for x = 0, 0.2, 0.4, and 0.6, respectively. The Tm of these samples is shift to the left with decreasing frequency as indication of relaxor ferroelectric behavior. The samples with x = 0.8 and 1 show anomaly at 514 ¡ãC and 551 ¡ãC which correspond to the transition phase of four layers Aurivillius. Magnetic properties for all samples containing Mn are paramagnetic. %K five layers aurivillius phase %K molten-salts %K relaxor ferroelectric %K paramagnetic %U http://journal.itb.ac.id/download.php?file=A10182.pdf&id=782&up=5