%T Fabrication of Morphology of One-dimensional Nano-|mAlOOH via Hydrothermal Route
%A LU Guang-Wei
%A YANG Qi
%A DENG Yi-Da
%A HU Wen-Bin
%J 无机材料学报
%D 2009
%I Science Press
%R 10.3724/sp.j.1077.2009.00463
%X One-dimensional nanostructure |mAlOOH was fabricated via hydrothermal synthesis. And the effects of the processing parameters on structure of |mAlOOH were investigated. The results show that |mAlOOH nanorod can be achieved on the condition that AlCl3 density is lower than 0.2mol/L, pH value of reacting solution is lower than 7, and reacting temperature is set between 160  nd 180 习when pH value is higher than 7, |mAlOOH is in the shape of nanoflake. Nanofiber with high slenderness ratio can be achieved on the condition that AlCl3 density is higher than 0.2mol/L, pH value is controlled between 5 and 6, and reacting temperature is set around 200  ith adding surfactant SDBS.
%K hydrothermal synthesis
%K nano-|mAlOOH
%K morphology
%K processing parameter
%U http://www.jim.org.cn/fileup/PDF/20090309.pdf