%0 Journal Article
%T Synthesis and Performance of Cathode Material Li3V2(PO4)3/C by Spray Drying and Carbothermal Method ￡¨SDATM￡
%A YU Feng
%A ZHANG Jing-Jie
%A YANG Yan-Feng
%A SONG Guang-Zhi
%J 无机材料学报
%D 2009
%I Science Press
%R 10.3724/sp.j.1077.2009.00349
%X Li-ion battery cathode material Li3V2(PO4)3/C composite was successfully prepared by spray drying and carbothermal method(SDCTM). The effect of spray drying was carefully studied. The structural, morphological and electrochemical properties were investigated by means of XRD, SEM, TEM and constant current chargea2discharge cycling. The results indicate that the sample prepared with spray drying twice at 260  nd subsequent heat-treating at 750  or 12h has better performance. Its average particle size is under 0.5| .It presents large reversible discharge capacity of 121.9, 114.6 and 104.6mAh ¤g-1 and excellent capacity retention rate closed to 100% after 50 cycles at C/5, 1C and 5C rate, respectively at the room temperature.
%K Li3V2(PO4)3/C
%K cathode material
%K spray drying
%K carbothermal method
%U http://www.jim.org.cn/fileup/PDF/20090230.pdf