%0 Journal Article
%T Influence of Temperature on Oxidation Resistance of Carbon/Carbon Composites Modified by a Hydrothermal Treatment
%A WANG Ni-Na
%A HUANG Jian-Feng
%A CAO Li-Yun
%A WU Jian-Peng
%J 无机材料学报
%D 2009
%I Science Press
%R 10.3724/sp.j.1077.2009.00948
%X Carbon/carbon (C/C) composites are one of the most important high temperature structure materials; Which are oxidized remarkably above 400  n oxidative atmosphere. In order to improve the oxidation resistance of C/C composites, suspension mixtures prepared by mixing B4C, SiC and Al2O3 powders and phosphoric acid solution were used as precursors to modify the C/C composites by a novel hydrothermal treatment. The influences of the hydrothermal treatment temperature on the phase, microstructure and antia2oxidation property of the as-modified composites were investigated. The asa2modified C/C composites were characterized by X-ray diffraction, scanning electron microscope (SEM), energy dispersive spectroscope (PDS) and X-ray photoelectron spectroscopy (XPS) techniques. Results show that the surface of the C/C composites is covered by a coating composed of molten B2O3, HPO3 and microcrystalline Al(PO3)3 after modified by the hydrothermal treatment, and their oxidation resistance is effectively improved in the temperature range from 120  o 200  The anti-oxidation property of the treated C/C composites is improved with increasing hydrothermal treatment temperature. The mass of the modified C/C composites losses only 2.31% after oxidized at 700  n air for 10h.
%K carbon/carbon composites
%K oxidation
%K hydrothermal
%K matrix modification
%U http://www.jim.org.cn/fileup/PDF/20090515.pdf