%0 Journal Article
%T Desempe o de recubrimientos base cinc en un ambiente tropical de elevada agresividad Performance of zinc-based coatings in a tropical marine atmosphere of high agressiveness
%A Orlando Salas
%J Revista T谷cnica de la Facultad de Ingenier赤a Universidad del Zulia
%D 2008
%I Scientific Electronic Library Online
%X El objetivo de esta investigaci車n es estudiar el efecto de diferentes aplicaciones de recubrimiento base cinc (galvanizado discontinuo, termorrociado por arco el谷ctrico y llama) en un ambiente marino-costero tropical, durante 24 meses de exposici車n. Para 谷sto, se evaluaron l芍minas de acero al carbono (SAE 1010) de 10 cm ℅ 5cm ℅ 3mm, recubiertas con cinc por los tres procesos. Las probetas se caracterizaron mediante espesor de recubrimiento, microestructura y porosidad, evalu芍ndose mensualmente por inspecci車n visual y registro fotogr芍fico. Luego de 24 meses de exposici車n, 谷stas fueron retiradas y analizadas en el laboratorio mediante medici車n de espesor remanente del recubrimiento, morfolog赤a de los productos de corrosi車n y an芍lisis microsc車pico del 芍rea transversal. Los resultados muestran que las velocidades de corrosi車n del cinc para todos los sistemas, sobrepasan el valor m芍ximo establecido en las normas ISO 9223(mayor de C5), adem芍s de ser muy sensible a la corrosi車n-erosi車n resultando inapropiados en este medio de exposici車n. The objective of this research is to study the effect of different applications on the behavior of zinc based coatings (discontinuous galvanized, thermal sprayed by electrical arc and flame processes) exposed to a tropical marine atmosphere during 24 months. For this, coupons of carbon steel (SAE 1010) of 10 cm ℅ 5cm ℅ 3mm were evaluated, covered with zinc by the three processes. The sheets were characterized by means of coat thickness, microstructure, and porosity, being evaluated monthly by visual inspection and photographic record. After 24 months of exposure, they were withdrawn and analyzed in the laboratory by measuring the thickness of the coating remaining, morphology of the corrosion products and microscopic analysis of the cross-sectional area. The results show that the zinc corrosion rates for all systems, exceed the maximum established in ISO 9223 (> C5), besides being very sensitive to corrosion-erosion resulting inappropriate in this type of atmospheres.
%K Galvanizado
%K termorrociado de Cinc por llama y arco el谷ctrico
%K corrosi車n atmosf谷rica
%K atm車sferas marinas tropicales
%K Galvanized
%K thermal sprayed zinc
%K atmospheric corrosion
%K tropical marine atmospheres
%U http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0254-07702008000400008