%0 Journal Article
%T Degradaci車n oxidativa asistida por microondas de lignina con per車xido de hidr車geno y sus propiedades tensoactivas Microwave assisted oxidative degradation of lignin with hydrogen peroxide and its tensoactive properties
%A Miguel Infante
%A Fredy Ysambertt
%A Mar赤a Hern芍ndez
%A Betsy Mart赤nez
%J Revista T谷cnica de la Facultad de Ingenier赤a Universidad del Zulia
%D 2007
%I Scientific Electronic Library Online
%X En el presente trabajo se estudiaron las propiedades tensoactivas de las fracciones obtenidas mediante degradaci車n oxidativa asistida por microondas con per車xido de hidr車geno de dos ligninas de pino (LAA y LKM). Las reacciones fueron llevadas a cabo en recipientes cerrados, empleando diferentes cantidades de agente oxidante, en un horno microondas dom谷stico. Las reacciones se completaron r芍pidamente, generando agua como subproducto. Los productos de oxidaci車n fueron caracterizados por espectroscopia UV-Vis y FTIR. Al compararlos con las muestras originales de lignina se observ車 una disminuci車n de la absorci車n cerca de los 280 nm debido a la oxidaci車n de los anillos arom芍ticos. En el an芍lisis por FTIR se observ車 el aumento de las se ales correspondientes a los grupos C=O entre 1.700-1.720 cm-1 y entre 1.650-1.700 cm-1 atribuidas a la oxidaci車n de las cadenas laterales y de los anillos arom芍ticos, respectivamente. Esto 迆ltimo se evidenci車 por la disminuci車n de la se al C=C arom芍tica, alrededor de los 1.600 cm-1. Se comprob車 la eficiencia y versatilidad de la radiaci車n microondas para promover este tipo de reacciones. Las ligninas oxidadas mostraron un aumento de la tensi車n superficial debido a la aparici車n de nuevos grupos polares. In this work the fractions obtained by microwave-assisted oxidative degradation with hydrogen peroxide of two pine lignins (LAA y LKM) and its tensoactive properties were studied. The reactions were carried out using different quantities of the oxidant agent in a domestic microwave oven in closed reactors. The reaction was completed quickly with the generation of water as by-product. The oxidation products were characterized by UV and FTIR spectroscopy. When comparing them with the original lignin samples in UV analysis, the absorption decreased near the 280nmdue to the oxidation of the aromatic rings. In the analysis by FTIR the signals corresponding to the groups C=O increased among 1,700-1,720 cm-1 and 1,650-1,700 cm-1 attributed to the oxidation of the lateral chains and aromatic rings, respectively. This results were evidenced because of the aromatic signal C=C around the 1,600 cm-1 decreased. It was proven the efficiency and versatility of the radiation microwaves to carry out this type of reactions. The surface tension of the oxidized lignin increased due the new hydrophilic groups.
%K Degradaci車n oxidativa
%K lignina
%K per車xido de hidr車geno
%K microondas
%K tensi車n superficial
%K Hydrogen peroxide
%K lignin
%K microwave
%K oxidative degradation
%K surface tension
%U http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0254-07702007000400014