%0 Journal Article
%T Evaluaci車n de la resistencia a la corrosi車n erosi車n de recubrimientos multicapas de TiN/AlTiN Evaluation of resistance to erosion corrosion of multilayer TiN/AlTiN
%A Willian Aperador
%A Cesar Amaya
%A Jorge Bautista Ruiz
%J Revista Latinoamericana de Metalurgia y Materiales
%D 2012
%I Universidad Sim車n Bol赤var
%X Se depositaron pel赤culas delgadas en forma de multicapas de TiN/AlTiN con periodos de 2, 6, 12 y 24 bicapas sobre sustratos de acero AISI 1045 mediante un sistema magnetr車n sputtering con r.f reactivo a partir de blancos de Ti y Al de alta pureza (99,99%) en una atm車sfera compuesta de Ar/N2. Las multicapas fueron evaluadas frente a fen車menos de corrosi車n, erosi車n y corrosi車n erosi車n a un 芍ngulo de impacto de 90o, y una soluci車n compuesta por NaCl 0,5 M y s赤lice, analizando el efecto del n迆mero de bicapas en la resistencia a la corrosi車n de estos recubrimientos. La caracterizaci車n electroqu赤mica se realiz車 mediante la t谷cnica curvas de polarizaci車n Tafel y la caracterizaci車n miscroestructural mediante microscop赤a electr車nica de barrido. Se encontr車 una disminuci車n notable en la velocidad de corrosi車n del sustrato, pasando de 2291,05 mpy a 351,24 mpy con la deposici車n de los recubrimientos con 2 bicapas y a un valor de 15,01 mpy para la muestra recubierta con 24 bicapas. Estos resultados corroboran el buen desempe o de las bicapas en la resistencia a la corrosi車n erosi車n. A partir de los resultados de microscop赤a electr車nica de barrido es posible ratificar el efecto protector de los recubrimientos sobre el sustrato en funci車n del incremento del n迆mero de bicapas. Thin films were deposited in multilayer TiN / AlTiN with periods of 2, 6, 12 and 24 bi-layers on AISI 1045 steel substrates, by RF magnetron sputtering system on Ti and Al targets (99.99%) in Ar/N2 atmosphere. The multi-layers were tested against to corrosion, erosion and corrosion erosion 90∼ angle impact and 0.5 M NaCl solution and silica, and analyzing the effect of number of bi-layers on the corrosion resistance of these coatings. The electrochemical characterization was performed by Tafel polarization curves and micro-structural by scanning electron microscopy. The study showed decreased rate corrosion on substrate, it diminished from 2291.05 mpy to 351.24 mpy with 2 bi-layers, and 15.01 mpy with 24 bi-layers. These results corroborate the good acting of the bi-layers in the corrosion erosion resistance. From the results of scanning electron microscopy can confirm the protective effect of coatings on the substrate as well as the increasing number of bi-layers.
%K Nitruro de titanio- aluminio
%K corrosi車n din芍mica
%K corrosi車n erosi車n
%K erosi車n
%K Microscop赤a electr車nica de barrido
%K aluminum titanium nitride
%K corrosion dynamics
%K erosion corrosion
%K erosion
%K scanning electron microscopy
%U http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0255-69522012000200007