%T Producci車n y caracterizaci車n de pel赤culas de 車xido de circonio por espray pir車lisis Production and characterization of zirconium oxide coatings by spray pyrolysis
%A Ivonne Cubillos
%A Jhon Jairo Olaya
%A Manuel Bethencourt
%A Gustavo Cifredo
%J Revista Latinoamericana de Metalurgia y Materiales
%D 2013
%I Universidad Sim車n Bol赤var
%X Se produjeron y caracterizaron pel赤culas de 車xido de zirconio sobre siete sustratos diferentes: vidrio, silicio (100) y cinco tipos de acero inoxidable AISI 304, 304LS, 316L, 321 y 2205. Los recubrimientos fueron depositados por el m谷todo de espray pir車lisis ultras車nico y se analiz車 el efecto de algunas variables de dep車sito, tales como temperatura del substrato, relaci車n de flujos de arrastre/direcci車n y tiempo de dep車sito. Las fases depositadas se identificaron mediante difracci車n de rayos X y la morfolog赤a por microscop赤a de fuerza at車mica y microscop赤a electr車nica de barrido. El an芍lisis de fases del acero y del recubrimiento se realiz車 mediante refinamiento Rietveld, y la composici車n qu赤mica a partir de espectroscopia de fotoelectrones de rayos X. Los resultados muestran pel赤culas homog谷neas, con alta reproducibilidad en la estructura cristalina tetragonal y estabilidad en el tiempo. Los recubrimientos depositados sobre el acero AISI 316L presentaron la mayor orientaci車n en el plano (101), mientras que en los otros sustratos la orientaci車n fue mixta. On this work were grown and characterized thin films of zirconium oxide on seven different substrates: common glass, silicon (100) and stainless steel AISI 304, 304LS, 316L, 321 y 2205. The coatings were deposited by ultrasonic spray pyrolysis technique and the effect of some deposit variables was analyzed. Some of the variables were: substrate temperature, the flow ratio of impact and drag, and deposition time. Deposited phases identification was carried out by Xray diffraction scanning electron microscopy and atomic force microscopy. The phase analysis of steel and coating was performed by Rieltveld refinement and surface chemical analysis performed by X-ray Photoelectron Spectroscopy. The results show homogeneous films, with high reproducibility in the tetragonal crystalline structure and shows stability over time. The coatings deposited on 316L steel showed a higher orientation in the plane (101), while the other substrates show mixed orientation.
%K acero inoxidable
%K circona
%K espray pir車lisis
%K microestructura
%K stainless steel
%K zircona
%K spray pyrolysis
%K microstructure
%U http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0255-69522013000100013