%0 Journal Article
%T S赤ntesis, caracterizaci車n estructural y magn谷tica de la aleaci車n CuAl0.67Cr0.33S2 Synthesis, structural and magnetic characterization of the alloy CuAl0.67Cr0.33S2
%A Manuel A Villarreal
%A Pedro Grima
%A Miguel Quintero
%A Ekadink Moreno
%J Revista Latinoamericana de Metalurgia y Materiales
%D 2012
%I Universidad Sim車n Bol赤var
%X En este trabajo se reporta la s赤ntesis, la caracterizaci車n estructural y la caracterizaci車n magn谷tica de la aleaci車n CuAl0.67Cr0.33S2. La muestra fue sintetizada utilizando la t谷cnica de fusi車n directa de los elementos constituyentes. El an芍lisis qu赤mico (EDX) permiti車 establecer las relaciones estequiom谷tricas para esta aleaci車n. El patr車n de difracci車n de polvo fue indexado y la fase principal cristaliza con simetr赤a tetragonal y par芍metros de celda unidad a = 5.3410(1)  , c = 10.4154(2)  . Este material es isomorfo con la estructura calcopirita que cristaliza en el grupo espacial Las medidas de susceptibilidad magn谷tica y resonancia paramagn谷tica electr車nica, en funci車n de la temperatura, fueron realizadas en un magnet車metro SQUID y en un espectr車metro BRUKER EMX de banda X, respectivamente. La aleaci車n exhibe un ordenamiento Ferrimagn谷tico con una temperatura de N谷el ~ 40 K. El ancho de l赤nea EPR muestra un comportamiento paramagn谷tico entre 100 y 600 K, mientras que el campo de resonancia y el factor g muestran una ligera variaci車n con la temperatura. This paper reports the synthesis, structural and magnetic characterization of the alloy CuAl0.67Cr0.33S2. The sample was synthesized using the technique of direct fusion of the constituent elements. Chemical analysis (EDX) allowed establishing the stoichiometric ratios for this alloy. The powder diffraction pattern was indexed and the main phase crystallizes with tetragonal symmetry and unit cell parameters a = 5.3410(1)  , c = 10.4154(2)  . This material is isomorphic with the chalcopyrite structure which crystallizes in space group Measurements of magnetic susceptibility and electronic paramagnetic resonance, depending on temperature, were performed in a SQUID magnetometer and a Bruker EMX Xband, respectively. The alloy exhibits a ferrimagnetic ordering with N谷el temperature ~ 40 K. The EPR linewidth shows a paramagnetic behavior between 100 and 600 K, while the resonance field and the g factor show a slight variation with temperature.
%K Semiconductores Magn谷ticos Diluidos
%K Difracci車n de rayos-X
%K Susceptibilidad Magn谷tica
%K Resonancia Paramagn谷tica Electr車nica
%K Dilute Magnetic Semiconductors
%K X-ray Diffraction
%K Magnetic Susceptibility
%K Electron Paramagnetic Resonance
%U http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0255-69522012000200016