%0 Journal Article
%T Influencia de la basicidad y composici車n ani車nica cromato-bromuro en la s赤ntesis del sistema cancrinita - sodalita Influence of basicity and chromate-bromide anionic composition in the synthesis of the cancrinite-sodalite system
%A Freddy Ocanto
%A Elizabeth Florenzano
%A Carlos F Linares
%J Revista Latinoamericana de Metalurgia y Materiales
%D 2013
%I Universidad Sim車n Bol赤var
%X La influencia de la basicidad y la composici車n ani車nica (CrO4(2-) y Br-) fue estudiada en la s赤ntesis de zeolitas de cromatocancrinita y bromosodalita. La s赤ntesis se llev車 a cabo partiendo de zeolita X como fuente de Si y Al, diferentes concentraciones de NaOH (8, 12 y 16 M) y proporciones variables en peso [NaBr/(NaBr + K2CrO4)] = 0,00; 0,25; 0,50; 0,75 y 1,00, de manera tal que la cantidad total de gramos fuera de 1,5 g. La s赤ntesis se realiz車 a 80 ∼C y presi車n aut車gena durante 40 h. Los cristales obtenidos fueron caracterizados por espectroscop赤a de infrarrojo con transformada de Fourier (IR-TF), difracci車n de rayos X en polvo (DRX) y cualitativamente por el color de los productos obtenidos. Los resultados se alaron que la bromosodalita se obtuvo a 100 y 75% en Br- y a todas las concentraciones de base empleadas; a 50% Br-, se obtuvo una mezcla entre cromato-cancrinita y bromosodalita; al utilizar 25 y 0% Br- se evidencia s車lo la presencia de la cromato-cancrinita. Estos resultados infieren que los productos obtenidos utilizando este par ani車nico en particular (bromosodalita o cromato-cancrinita) dependen de las composiciones en peso de cada ani車n en el gel de reacci車n y no del medio b芍sico de la reacci車n. The influence of the basicity and anionic composition (CrO4(2-) and Br-) was studied in the synthesis of chromate-cancrinite and bromosodalite-type zeolites. The synthesis was carried out starting from zeolite X as a source of Si and Al, different concentrations of NaOH (8, 12 and 16 M) and variable weight proportions [NaBr / (NaBr + K2CrO4)] = 0.00, 0, 25, 0.50, 0.75 and 1.00, so that the total grams was 1,5 g. The synthesis was performed at 80∼ C and autogenous pressure for 40 h. Obtained crystals were characterized by Fourier transformed infrared spectroscopy (FT-IR), powder X-ray diffraction (XRD) and qualitatively by the color of the products obtained. Results showed that the bromosodalite was obtained at 100 and 75% Br- for all used base concentrations; at 50% Br-, a mixture of chromate-cancrinite and bromosodalite was determined. When 25 and 0% Br- was used, chromate-cancrinite was only determined. These results infer that obtained products for this particular anion pair (chromate-cancrinite or bromosodalite) depends on the compositions by weight of each anion in the reaction gel and not the employed base concentration.
%K basicidad
%K bromosodalita
%K cromato-cancrinita
%K zeolitas
%K basicity
%K bromosodalite
%K chromate-cancrinite
%K zeolites
%U http://wwww.scielo.org.ve/scielo.php?script=sci_arttext&pid=S0255-69522013000100014