%T Comportamiento de paneles de bamb¨² guadua laminado ante cargas paralelas al plano The structural behaviour of laminated-guadua panels under parallel plane loads
%A Pinilla Rodr¨ªguez Juan Jacobo
%A Takeuchi Tam Caori Patricia
%J Ingenier¨ªa e Investigaci¨®n
%D 2012
%I Universidad Nacional de Colombia
%X Como un primer paso en el estudio del comportamiento ante cargas s¨ªsmicas de p¨®rticos de bamb¨² guadua laminados con paneles del mismo material, el Grupo de Investigaci¨®n ¡°An¨¢lisis, Dise o y Materiales, GIES¡±, de la Universidad Nacional de Colombia, ensay¨® dos tipos de paneles elaborados con bamb¨² Guadua angustifolia Kunth y poli (vinil acetato), PVA: los paneles tipo 1 de secci¨®n transversal maciza y los paneles tipo 2 de secci¨®n transversal tipo s¨¢ndwich. Se consideraron tres alturas para cada tipo de panel y se ensayaron diez r¨¦plicas por altura y por tipo, para un total de sesenta ensayos. Para cada uno de los paneles ensayados se realiz¨® una curva carga-desplazamiento. Los paneles tipo 1, con altura de 0,34 m y 0,63 m, mostraron un comportamiento el¨¢stico inicial seguido de un comportamiento inel¨¢stico, mientras que los paneles tipo 1 y 2 de 0,98 m de altura revelaron un comportamiento casi totalmente el¨¢stico hasta la falla. Todos los paneles sufrieron aplastamiento en la base; sin embargo, el principal mecanismo de falla fue el alabeo. The Universidad Nacional de Colombia "Analysis, Design and Materials - GIES" research group tested two types of panels made from Guadua angustifolia Kunth and poly vinyl acetate (PVA) as a first step in studying the behaviour of laminated guadua frames having panels of the same material under seismic load: type 1 panels had a solid cross-section and type 2 panels a sandwich cross-section. Each type of panel had three different heights and 10 replicates were tested for each type and height (60 trials in total). Each panel¡¯s load compared to displacement curve was found; 0.34m and 0.63m type1 panels had initial elastic behaviour followed by inelastic behaviour while 0.98 m panels made of both types had an almost completely elastic behaviour until failure. All panels became crushed at their base; however, the main failure mechanism was warping.
%K bamb¨² Guadua angustifolia
%K laminados
%K rigidez
%K ductilidad
%K resistencia