%0 Journal Article
%T Obtenci車n y Caracterizaci車n de Revestimientos Protectores a Base de Silanos para la Protecci車n de Aceros Galvanizados Obtention and Characterization of Silane based Films for the Protection of Galvanized Steel
%A Sandra R Kunst
%A Jos谷 F Matos
%A Matias A Korb
%A C谷lia F Malfatti
%J Informaci車n Tecnol車gica
%D 2011
%I Centro de Informaci車n Tecnol車gica
%X Se presenta un estudio del comportamiento de pel赤culas de silanos Gamma-Aminopropyl tirethoxysilano y del N-(Beta-Aminoethyl)-Gamma-Aminopropyl trimethoxysilano aplicados por el proceso de revestimiento por inmersi車n (dip-coating) sobre el acero galvanizado. Se usan los mecanismos de curado t谷rmico y curado por irradiaci車n ultravioleta. Los substratos y revestimientos a base de zinc reciben normalmente un tratamiento de superficie para mejorar la resistencia a la corrosi車n, pero usan cromo hexavalente que presenta un elevado grado de toxicidad. Las pel赤culas polim谷ricas conteniendo silanos organofuncionales surgen como alternativa para la pasivaci車n de substratos a base de zinc. Los revestimientos de silano obtenidos fueron evaluados a partir de ensayos electroqu赤micos y 芍ngulos de mojabilidad y la morfolog赤a fue caracterizada por microscop赤a electr車nica de barrido. Los resultados muestran que las pel赤culas elaboradas presentan una cobertura homog谷nea y que el tipo de silano empleado tiene influencia en la formulaci車n y en los par芍metros de curado. This work presents a study on the behavior of silane films Gamma-Aminopropyl triethoxysilane and N-(beta-aminoethyl)-gamma-Aminopropyl trimethoxysilane, obtained by dip-coating process on galvanized steel. The films were cured by thermal and ultraviolet irradiation cure processes. The substrates and zinc-based coatings are usually employed as surface treatment to improve the corrosion resistance but they employ hexavalent chromium that has a high degree of toxicity. Polymer films containing organofunctional silanes have been studied as an alternative to the passivation of zinc-based substrates. The silane coatings were evaluated by electrochemical tests and contact angle. The film morphology was characterized by scanning electron microscopy. The results showed that the films obtained presented a homogeneous coverage and that the influence of silane employed in the formulation was evident, as well as the cure parameters.
%K acero galvanizado
%K silano
%K corrosi車n
%K curado por ultravioleta
%K galvanized steel
%K silane
%K corrosion
%K ultraviolet irradiation cure