%T Interaction of RuO<sub>2</sub> and Lead-Silicate Glass in Thick-Film Resistors
%A Gulmurza Abdurakhmanov
%A Gulbahor S. Vakhidova
%A Lutfullo X. Tursunov
%J World Journal of Condensed Matter Physics
%P 1-5
%@ 2160-6927
%D 2011
%I Scientific Research Publishing
%R 10.4236/wjcmp.2011.11001
%X Results of investigation of X-ray diffraction, infrared and optical spectra of powders of the ruthenium dioxide, lead-silicate glass as well as their mixture before and after sintering are reported. Sintering conditions typical for thick film resistors were used. Intensity of main lines of RuO<sub>2</sub> in X-ray diffraction patterns of sintered mixtures decreases and they slightly shift towards small angles. No new reflexes appear in these patterns. Absorbance of RuO<sub>2</sub> in the range of 2.5-100 ¦Ìm is proportional to   and featureless. Infrared spectrum of lead-silicate glass has absorption bands of [SiO4]4- tetrahedra and Pb-O bonds only. Optical spectrum of RuO2 has wide absorption bands at 950 and 370 nm. Spectra of the mixture of RuO<sub>2</sub> and glass powders before and after sintering are different indicating that there is interaction between them during the sintering process. Concentration of free charge carriers estimated from the optical spectra is about 1021 cm-3.
%K Ruthenium Dioxide
%K Lead-Silicate Glass
%K Thick Film Resistors
%K Infra Red And Optical Spectra
%K X-Ray Diffraction
%U http://www.scirp.org/journal/PaperInformation.aspx?PaperID=3952