%0 Journal Article
%T Incidencia del recocido bajo atm車sfera de nitr車geno en el tama o de grano, textura y p谷rdidas en el n迆cleo (10-1000 Hz) en cintas microcristalinas Fe - 6,4 % Si obtenidas por solidificaci車n r芍pida
%A Ibarrondo
%A I.
%A Degauque
%A J.
%A Recarte
%A V.
%A San Juan
%A J. M.
%J Revista de Metalurgia
%D 1998
%I Consejo Superior de Investigaciones Cient赤ficas
%X In the present research, high silicon (6.4%) - iron microcrystalline ribbons were obtained by rapid quenching. In this material the incidence of the atmosphere (N2) and the annealing temperature (900-1,100∼C) on the micrographic structure, grain size and texture and, as a consequence, in the total core losses ((1.0 T) 10-1000 Hz) were studied. The analysis of the results shows that the core losses are, in all cases, lower than those of the highest grade of conventionally processed nonoriented magnetic steel sheets, this becoming specially noticeable in the frequency range between 50-400 Hz. En el presente trabajo se describe la obtenci車n de cintas microcristalinas Fe - 6,4 % Si por solidificaci車n r芍pida. Sobre el material as赤 obtenido, se estudi車 el efecto que la atm車sfera (N2) y la temperatura de recocido (900-1100∼C) ejercen en la estructura microgr芍fica, tama o de grano y textura inducida y, en consecuencia, en la cifra de p谷rdidas totales ((1,0 T) 10-1000 Hz.). Los resultados obtenidos muestran, en todos los casos, una cifra de p谷rdidas inferior al mejor grado de la chapa magn谷tica no orientada procesada convencionalmente. Esto adquiere especial relieve en el intervalo de frecuencias comprendido entre 50-400 Hz.
%K Rapid quenching
%K High silicon magnetic steel sheets
%K Annealing cycle
%K Grain size
%K Textures
%K Core losses
%K Solidificaci車n r芍pida
%K Chapa magn谷tica de alto contenido de silicio
%K Tratamiento t谷rmico
%K Tama o de grano
%K Texturas
%K Cifra de p谷rdidas
%U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/755/767