%T Efecto del silicio como posible elemento reactivo en la protecci車n frente a la oxidaci車n a elevada temperatura del acero inoxidable AISI 304
%A Otero
%A E.
%A P谷rez
%A F. J.
%A Hierro
%A M. P.
%A G車mez
%A C.
%J Revista de Metalurgia
%D 1998
%I Consejo Superior de Investigaciones Cient赤ficas
%X The influence of silicon incorporated into the alloy by means of ion implantation of 1 x 1015 ions/cm2 at 150 keV on the protective scale development based upon Cr1,3Fe0,7O3 and manganese-enriched spinels, Mn1,5Cr1,5O4 after oxidation of an austenitic AISI 304 stainless steel at 1,173 K and atmospheric pressure of air for 144 h has been studied. The presence of small quantities of silicon at the outermost layers of the alloy promotes transport of chromium during the early stages of oxidation. Further, ion implantation seems to play a beneficial role against decarburization of the alloy. Se estudia la influencia de silicio incorporado a la aleaci車n mediante implantaci車n i車nica de 1 x 1015 iones/cm2 a 150 keV en el crecimiento de la capa protectora de oxidaci車n basada en Cr1,3Fe0,7O3 y en espinelas enriquecidas en manganeso, Mn1,5Cr1,5O4, tras someter a un acero inoxidable austen赤tico AISI 304 a oxidaci車n a 1.173 K y presi車n atmosf谷rica de aire durante 144 h. La presencia de peque as cantidades de silicio en las capas m芍s externas del material promueve el transporte de cromo durante los primeros estadios de la oxidaci車n. Adem芍s, la implantaci車n i車nica parece ejercer un efecto beneficioso contra la descarburaci車n de la aleaci車n.
%K High temperature oxidation
%K Stainless steel
%K Ionic implantion
%K Oxidaci車n a alta temperatura
%K Acero inoxidable
%K Implantaci車n i車nica