%0 Journal Article %T Caracterizaci車n de capas coloreadas sobre AISI 304 %A L車pez %A J. %A Blanco %A E. %A Botella %A J. %A Esquivias %A L. %J Revista de Metalurgia %D 1998 %I Consejo Superior de Investigaciones Cient赤ficas %X A common method for obtaining colour coatings on stainless steel surfaces is by dipping in strongly oxidizing solutions (H2SO4-CrO3) at 70∼C. This work improves the knowledge of these coatings by means of techniques that were not available some years ago, such as ellipsometry, to determine the refraction index and the thickness, and atomic field microscopy (AFM), to observe the coloured surface. From these techniques, it is possible to state that films are formed by an aggregation of particle ranging in size from 5 to 15 nm, the interstices are pores of approximately 5 nm diameter. El m谷todo m芍s usual de obtener en la superficie de los aceros inoxidables capas de colores variables es mediante su inmersi車n en soluciones fuertemente oxidantes (H2SO4-CrO3) a una temperatura en torno a 70∼C. El trabajo mejora el conocimiento que de estas capas se tiene por medio de t谷cnicas que no eran disponibles hace algunos a os, tales como la elipsometr赤a, para la obtenci車n de par芍metros 車pticos y determinaci車n de espesores, y la microscop赤a de campo at車mico, para la observaci車n de la superficie coloreada. El uso conjunto de estas t谷cnicas permite observar que la pel赤cula de color est芍 formada por una agregaci車n de part赤culas con un tama o que oscila entre los 5 y los 15 nm, los intersticios que aparecen entre las part赤culas pueden identificarse como poros de unos 5 nm de tama o. %K Anticorrosive coating %K AISI 304 %K Ellipsometry %K Colouring %K Recubrimiento anticorrosivo %K AISI 304 %K Elipsometr赤a %K Coloreado %U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/719/731