%T Influencia de los elementos residuales cobre, esta o, f車sforo y ars谷nico en el agrietamiento de la superficie del acero inoxidable 18-8 durante la compresi車n a altas temperaturas
%A Botella
%A J.
%A Fern芍ndez
%A M. T.
%A Fern芍ndez de Castillo
%A I.
%J Revista de Metalurgia
%D 1998
%I Consejo Superior de Investigaciones Cient赤ficas
%X The effect of certain different concentrations of Cu, Sn, P and As on the surface cracking of 18-8 austenitic stainless steel hot compressed specimens has been studied, at 1,123 and 1,273 K, in an oxidizing atmosphere (air). A procedure for determining surface cracking has been established, and the cracking factor obtained in this way is correlated with the chemical composition of the materials at both temperatures. The cracking factors obtained at 1,273 K have been compared with the reduction of area drops obtained by hot tension tests at the same temperature. Esta investigaci車n aborda el estudio del efecto de concentraciones variables de cobre, esta o, f車sforo y ars谷nico en el agrietamiento de la superficie de un acero 18-8, sometido a ensayos de compresi車n, a 1.123 y 1.273 K, en atm車sfera oxidante (aire). Se desarrolla un procedimiento de cuantificaci車n del grado de agrietamiento y se relaciona cada 赤ndice de agrietamiento as赤 obtenido, a las distintas temperaturas, con la composici車n qu赤mica" de los materiales. Los 赤ndices de agrietamiento correspondientes a los materiales comprimidos a 1.273 K se comparan con los valores de p谷rdida de reducci車n de 芍rea obtenidos mediante ensayos de tracci車n a la misma temperatura.
%K Austenitic stainless steel
%K Copper
%K Tin
%K Phosphorous
%K Arsenic
%K Surface cracking
%K Acero inoxidable austen赤tico
%K Cobre
%K Esta o
%K F車sforo
%K Ars谷nico
%K Agrietamiento superficial
%U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/699/711