%0 Journal Article %T Influencia de los tratamientos de revenidos intercr¨ªticos en la concentraci¨®n de n¨ªquel correspondiente, a part¨ªculas de austenita residual en un acero con 9% Ni %A Casarin %A S. J. %A Kestenbach %A H-J. %A Valencia %A E. %J Revista de Metalurgia %D 1999 %I Consejo Superior de Investigaciones Cient¨ªficas %X Retained austenite particles with nanometric dimensions in 9 % nickel steels microstructures were observed after different intercritical tempering treatments ranged between 540 ¡ãC and 670 ¡ãC corresponding to the (¦Á + ¦Ã) two-phase field of Fe-Ni diagram. The thermal stability of particles turned out to be strongly influenced by its nickel contents and gradients of this element. The gradients were dependent on time and temperature of tempering. En la estructura fina de aceros con 9% Ni, despu¨¦s de diferentes tratamientos t¨¦rmicos de revenido a temperaturas entre 540-670¡ãC correspondiente al campo bif¨¢sico (¦Á + ¦Ã) del diagrama Fe-Ni se observaron part¨ªculas de dimensiones nanom¨¦tricas de austenita residual. La estabilidad t¨¦rmica de estas part¨ªculas result¨® ser fuertemente influenciada por la concentraci¨®n de n¨ªquel contenida en ellas. En este sentido fueron observados gradientes de concentraci¨®n de n¨ªquel en las mismas dependiendo ¨¦stos del tiempo y la temperatura de revenido. %K Retained austenite. 9 % Ni steel %K Intercritical tempering treatment %K Microanalysis %K Austenita residual %K Acero 9 % Ni %K Revenido %K Microan¨¢lisis %U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/618/628