%0 Journal Article
%T Efecto de la modificaci車n superficial de alambres delgados de acero inoxidable AISI 302 mediante plasma electrol赤tico sobre sus propiedades mec芍nicas
%A Gallegos
%A A.
%A Camurri
%A C.
%A Carrasco
%A C.
%A Soldera
%A F.
%J Revista de Metalurgia
%D 2012
%I Consejo Superior de Investigaciones Cient赤ficas
%X In this work different tests using electrolytic plasma (EP) on thin wires of stainless steel AISI 302 in an inert solution were performed. Tensile tests were carried out in order to measure changes in the mechanical strength of the samples; moreover, both the morphological and microstructural changes also were evaluated. It was found that after 10 s of the application of EP, the samples surface was uniformly covered by nodules-like and craters similar to those found in the melting and cooling periods of EP. The results show a significant surface grain refinement, leading to crystalline arrangements with sizes less than 200 nm and also an increase in the samples tensile strength of at least 57 % respect to steel base. En este trabajo se realizaron ensayos de aplicaci車n de plasma electrol赤tico (PE) sobre alambres delgados de acero inoxidable AISI 302 en una soluci車n inerte. Las probetas se sometieron a ensayos de tracci車n, con el fin de medir cambios en su resistencia mec芍nica; adicionalmente fueron evaluadas en sus cambios morfol車gicos y microestructurales. Se encontr車 que despu谷s de 10 s de aplicaci車n de PE, la superficie de las probetas estaba uniformemente cubierta por n車dulos y cr芍teres propios del ciclo de fusi車n y enfriamiento del PE; se evidenci車 un significativo afinamiento del grano superficial, llegando a ordenamientos cristalinos de tama o menor a 200 nm y tambi谷n se observ車 que la capa superficial afectada present車 un incremento de la resistencia a la tracci車n de al menos un 57 % respecto al acero base.
%K Electrolytic plasma technology (EPT)
%K Contact glow discharge electrolysis (CGDE)
%K Surface nanostructuration
%K Nanograins
%K Rupture strength
%K Plasma electrolytic oxidation (PEO)
%K Plasma electrol赤tico
%K Electr車lisis de alto voltaje
%K Nanoestructuraci車n superficial
%K Nanogranos
%K Resistencia a la ruptura
%K Oxidaci車n por plasma electrol赤tico
%U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/1259/1270