%T Estudio del comportamiento de los recargues multicapas de dep車sitos soldados de fundici車n blanca al cromo
%A R. Collazo-Carceller
%A H L車pez Salinas
%J Revista de Ingenier赤a Mec芍nica
%D 2009
%I Instituto superior polit谷cnico Jos谷 Antonio Echeverr赤a / CUJAE
%X Se determina la influencia de los par芍metros Energ赤a introducida (Hi), N迆mero de capas (Nc) y Ancho del dep車sito (Ad), en la morfolog赤a y el incremento de la resistencia al desgaste abrasivo de capas depositadas sobre acero 1020 utilizando el electrodo de fundici車n blanca al cromo UTP Ledurit 每 61. Empleando la microscopia 車ptica se identificaron y cuantificaron las fases presentes, analizando su efecto en el desgaste. Siendo determinante la influencia de la inclinaci車n de las dendritas y su posici車n con respecto a 90∼ en el incremento de la resistencia al desgaste abrasivo. Se caracterizaron los posibles mecanismos de da o superficial provocado por desgaste abrasivo empleando la microscopia electr車nica de barrido. Se propusieron modelos lineales para correlacionar la influencia de la cantidad, tama o, dispersi車n de los carburos y el 芍ngulo de inclinaci車n de las dendritas, en el incremento de la resistencia al desgaste.The influence of different parameters in layer morphology and abrasion resistance of Fe-Cr-C electrodes UTP Ledurit 每 61 on steel 1020 was studied. Introduced Energy (Hi), Number of Layers (Nc), and Deposit Width (Ad) were the main parameters considered. The metallographic identification and quantification of metal phases and the determination of their effect in abrasion resistance were made with optical microscopy. The abrasive wear test characterized by scanning electron microscopy, defines a possible mechanism of surface damage. It was found that the angle formed between a normal line to the surface and the dendrite inclination is directly related with the increment of wear resistance. Lineal models that correlate wear resistance with quantity, size, and carbide dispersion and dendrite angle inclination were also developed.
%K morfolog赤a
%K desgaste abrasivo
%K par芍metros de soldadura
%K dendritas
%K modelomorphology
%K abrasive wear
%K welding parameters
%K dendrites
%K modelings